Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Industrial Laminates/Norplex NP130HF Glass Fabric

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP130HF Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: High flexural, impact and tensile strength glass fabric epoxy laminate, especially in the machine direction. Engineered to provide better physical properties than NEMA FR-4. More dimensionally stable than standard NP510A. Application is for "bed-of-nails" equipment for printed circuit board testing. MIL-I-24768/27, type GEE-F.Thickness Tested: 0.062", 0.125", & 0.500".
Physical Properties Metric English Comments
Specific Gravity 1.90 - 2.00 g/cc

@Thickness 1.57 mm
 1.90 - 2.00 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 0.13 %

@Thickness 1.57 mm
 0.13 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90 - 110

@Thickness 1.57 mm
 90 - 110

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 365 MPa

@Thickness 1.57 mm
 53000 psi

@Thickness 0.0620 in
 CW; ASTM D638
448 MPa

@Thickness 1.57 mm
 65000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 20.7 GPa

@Thickness 1.57 mm
 3000 ksi

@Thickness 0.0620 in
 CW; ASTM D229
25.5 GPa

@Thickness 1.57 mm
 3700 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 483 MPa

@Thickness 1.57 mm
 70000 psi

@Thickness 0.0620 in
 CW; ASTM D790
586 MPa

@Thickness 1.57 mm
 85000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 496 MPa

@Thickness 12.7 mm
 72000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 159 MPa

@Thickness 15.7 mm
 23000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 4.81 J/cm

@Thickness 12.7 mm
 9.00 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
6.94 J/cm

@Thickness 12.7 mm
 13.0 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 14.7 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 8.17 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 13.7 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 7.61 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 130 °C
266 °F
Glass Transition Temp, Tg 130 °C
266 °F
Tg
Flammability, UL94 V-0

@Thickness 1.57 mm
 V-0

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 4.8

@Thickness 1.57 mm
 4.8

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 27.6 kV/mm

@Thickness 1.57 mm
 700 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
35.4 kV/mm

@Thickness 1.57 mm
 900 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 60000 V

@Thickness 1.57 mm
 60000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
63000 V

@Thickness 1.57 mm
 63000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.022

@Thickness 1.57 mm
 0.022

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 75 sec

@Thickness 3.17 mm
 75 sec

@Thickness 0.125 in
 ASTM D495
Descriptive Properties Value Comments
Bond Strength 2500 lb
0.5", ASTM D229
Color Natural