Industrial Laminates/Norplex NP159 Synthetic Fabric  (discontinued **)

Category	Polymer , Thermoset , Aramid , Phenolic
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Industrial Laminates/Norplex NP159 Synthetic Fabric  (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: Woven aramid fiber fabric combined with high temperature phenolic resin. With a proper post baking procedure, NP159 will withstand continuous operation at 200° C. Material becomes brittle at this temperature and therefore, undo mechanical stress should be avoided.Thickness Tested: 0.062", 0.125" and 0.500"

Physical Properties	Metric	English	Comments
Specific Gravity	1.25 - 1.35 g/cc <br>@Thickness 1.57 mm	1.25 - 1.35 g/cc <br>@Thickness 0.0620 in	ASTM D792
Moisture Absorption at Equilibrium	1.3 % <br>@Thickness 1.57 mm	1.3 % <br>@Thickness 0.0620 in	ASTM D229

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	110 - 130 <br>@Thickness 1.57 mm	110 - 130 <br>@Thickness 0.0620 in	ASTM D785
Tensile Strength, Yield	64.1 MPa <br>@Thickness 1.57 mm	9300 psi <br>@Thickness 0.0620 in	CW; ASTM D638
	75.8 MPa <br>@Thickness 1.57 mm	11000 psi <br>@Thickness 0.0620 in	LW; ASTM D638
Modulus of Elasticity	4.14 GPa <br>@Thickness 1.57 mm	600 ksi <br>@Thickness 0.0620 in	CW; ASTM D229
	6.21 GPa <br>@Thickness 1.57 mm	900 ksi <br>@Thickness 0.0620 in	LW; ASTM D229
Flexural Strength	131 MPa <br>@Thickness 1.57 mm	19000 psi <br>@Thickness 0.0620 in	CW; ASTM D790
	200 MPa <br>@Thickness 1.57 mm	29000 psi <br>@Thickness 0.0620 in	LW; ASTM D790
Compressive Strength	310 MPa <br>@Thickness 12.7 mm	45000 psi <br>@Thickness 0.500 in	ASTM D695
Shear Strength	100 MPa <br>@Thickness 15.7 mm	14500 psi <br>@Thickness 0.620 in	ASTM D732
Izod Impact, Unnotched	2.83 J/cm <br>@Thickness 12.7 mm	5.30 ft-lb/in <br>@Thickness 0.500 in	CW, Cond E-48/50; ASTM D256
	3.31 J/cm <br>@Thickness 12.7 mm	6.20 ft-lb/in <br>@Thickness 0.500 in	LW, Cond E-48/50; ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	40.0 µm/m-°C <br>@Thickness 1.57 mm,<br> Temperature 20.0 °C	22.2 µin/in-°F <br>@Thickness 0.0620 in,<br> Temperature 68.0 °F	x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow	45.0 µm/m-°C <br>@Thickness 1.57 mm,<br> Temperature 20.0 °C	25.0 µin/in-°F <br>@Thickness 0.0620 in,<br> Temperature 68.0 °F	x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air	160 °C	320 °F
Flammability, UL94	HB <br>@Thickness 1.57 mm	HB <br>@Thickness 0.0620 in

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.8 <br>@Thickness 1.57 mm	3.8 <br>@Thickness 0.0620 in	Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength	21.7 kV/mm <br>@Thickness 1.57 mm	550 kV/in <br>@Thickness 0.0620 in	Cond D-48/50; ASTM D229 S.T.
	27.6 kV/mm <br>@Thickness 1.57 mm	700 kV/in <br>@Thickness 0.0620 in	Cond A; ASTM D229 S.T.
Dielectric Breakdown	35000 V <br>@Thickness 1.57 mm	35000 V <br>@Thickness 0.0620 in	Cond D-48/50; ASTM D229 S/S
	65000 V <br>@Thickness 1.57 mm	65000 V <br>@Thickness 0.0620 in	Cond A; ASTM D229 S/S
Dissipation Factor	0.035 <br>@Thickness 1.57 mm	0.035 <br>@Thickness 0.0620 in	Cond D-24/23; ASTM D150
Arc Resistance	200 sec <br>@Thickness 3.17 mm	200 sec <br>@Thickness 0.125 in	ASTM D495

Descriptive Properties	Value	Comments
Bond Strength	2400 lb	0.5", ASTM D229
Color	Natural