Nanocyl PLASTICYL™ PA1501 Polyamide 66 with 3 wt% Multi-Wall Carbon Nanotubes
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nanocyl |
| Trade Name | PLASTICYL™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nanocyl PLASTICYL™ PA1501 Polyamide 66 with 3 wt% Multi-Wall Carbon Nanotubes.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PLASTICYL™ is a family of Multi-Wall Carbon Nanotube (MWNT) thermoplastic concentrates for applications requiring superior electrical conductivity and electrostatic discharge (ESD) properties. PLASTICYL™ PA1501 is a conductive masterbatch based on polyamide 66. Because of its flow formulation, PLASTICYL™ PA1501 is ideal for standard injection molding and extrusion processes.Applications:ESD (Electrostatic Discharge) and electrically conductive partsE&E, automotive, industrialsInjection molding, extrusionBenefits:Electrical conductivity at low loadingRetention of key mechanical propertiesEasier processing
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 3 % | 3 % | Carbon Nanotube Loading |
| Melt Flow | 13.22 g/10 min @Load 1.20 kg, Temperature 300 °C |
13.22 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133:1997 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.18 MPa | 10030 psi | ISO 527-1,2 |
| Elongation at Break | 2.21 % | 2.21 % | ISO 527-1,2 |
| Tensile Modulus | 3.466 GPa | 502.7 ksi | ISO 527-1,2 |
| Charpy Impact, Notched | 0.285 J/cm² | 1.36 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | Masterbatch; ISO 11357-1,-3 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.12e+10 ohm-cm | 1.12e+10 ohm-cm | CTM E043 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 300 °C | 572 °F | Material Temperature |
| Mold Temperature | 80.0 °C | 176 °F | |
| Hold Pressure | 25.0 MPa | 3630 psi | |
| Back Pressure | 0.000 MPa | 0.000 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Processing: Holding Time | 25 s | |
| Processing: Injection Speed | 70 cm³/s | |
| Processing: Plasticizing Speed | 0.4 m/s |
Users viewing this material also viewed the following:
- Hyosung Topilene HJ700 PP
- Techmer ES Electrablend® PPS 05002
- Shandong Rike Chemical HELIâ„¢ HL-K200 PVC Processing Aid Series (PA)
- Lubrizol ESTANE® 58142 Ester Based Thermoplastic Polyurethane (European Grade)
- CRP Technology Windform® FX Polyamide Composite
- CMW® D154X Post-Oxidized Silver Cadmium Oxide Contact Material ASTM B781 Table 3
- Chi Mei Polylac® PA-758R ABS - Transparent
- Arlon 41580B030 0.030" Uncured, Unsupported Silicone Rubber on Release Carrier
- Overview of materials for Nylon 66, 40% Carbon Fiber Filled
- Overview of materials for Polypropylene with Glass Fiber + PTFE
Copyright © lookpolymers.com All Rights Reserved