NatureWorks® Ingeo™ 2003D General Purpose Transparent Extrusion Grade Biopolymer
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | NatureWorks LLC |
| Trade Name | Ingeo™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NatureWorks® Ingeo™ 2003D General Purpose Transparent Extrusion Grade Biopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NatureWorks® PLA polymer 2003D is a thermoplastic resin derived from annually renewable resources. PLA polymer 2003D processes easily on conventional extrusion equipment. Specifically designed for use in fresh food packaging and food serviceware applications. Ingeo biopolymer 2003D is a transparent general purpose extrusion grade that is used naturally or as part of a formulated blend. This is a high molecular weight biopolymer grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Viscosity Measurement | 4.0 @Temperature 30.0 °C |
4.0 @Temperature 86.0 °F |
1.0 g/dl in chloroform; Relative Viscosity |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 210 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ASTM D882 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D882 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D882 |
| Tensile Modulus | 3.61 GPa | 524 ksi | ASTM D882 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 3.83 GPa | 555 ksi | ASTM D790 |
| Izod Impact, Notched | 0.1600 J/cm | 0.2997 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 145 - 160 °C | 293 - 320 °F | Peak; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | ASTM E2092 |
| Glass Transition Temp, Tg | 55.0 - 60.0 °C | 131 - 140 °F | ASTM D3418 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | Thickness Unknown |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 180 °C | 356 °F | |
| Adapter Temperature | 200 °C | 392 °F | |
| Die Temperature | 190 °C | 374 °F | |
| Melt Temperature | 210 °C | 410 °F | |
| Drying Temperature | 90.0 °C @Time 7200 sec |
194 °F @Time 2.00 hour |
|
| Moisture Content | <= 0.025 % | <= 0.025 % | |
| Dew Point | -40.0 °C | -40.0 °F | |
| Drying Air Flow Rate | >= 14.2 l/min | >= 0.500 ft³/min (CFM) | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND 1076, Part A Silicone
- Lucent Polymers PBT-310 Polybutylene Terephthalate, 30% Glass Fiber/Mineral Reinforced, Low Warp
- Henkel Turco 4215 NC-LT Cleaner
- Solvay Specialty Polymers Amodel® AFA-6145 V0 Z Polyphthalamide (PPA), 45% Glass Fiber
- Solvay Specialty Polymers Xydar® G-930 Liquid Crystal Polymer (LCP), 30% Glass Fiber
- Teknor Apex APEX® 130 Polyvinyl Chloride, Flexible
- Borealis Borecene™ RM8343RC Linear Polyethylene for Rotational Molding
- A. Schulman POLYPUR™ FPU 1103F Thermoplastic Polyurethane Compound
- Hexcel® HexForce™ GA045 Carbon Fabric
- BASF Cyclohexylamine (CHA)
Copyright © lookpolymers.com All Rights Reserved