Petroquimica Triunfo Trithene® TX 4003 LDPE and LLDPE Blend - High Resistance Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , LLDPE
Manufacturer Petroquimica Triunfo
Trade Name Trithene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petroquimica Triunfo Trithene® TX 4003 LDPE and LLDPE Blend - High Resistance Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Trithene® TX 4003 resin is a blend of low-density polyethylene (LDPE) of high molecular weight with linear low-density polyethylene (LLDPE) designed for the production of industrial films. Since it presents gains in resistance in the weld region, this product meets the requirements of the cutting and welding line and/or of the automatic or semi-automatic packaging, contributing to the reduction of losses due to sacks breaking. The Trithene® TX 4003 resin presents excellent performance on conventional extruders for LDPE, ensuring thermal stability during the processing and allowing the production of films with good thickness uniformity. The components that form the product Trithene® TX 4003 complies with the requirements of Brazilian and corresponding legislation of Mercosul and it is in conformity with FDA Regulations 21 CFR 177.1520 (c) 2.1, to contact with foodstuff.Applications: Technical films for high resistance industrial packages and plastic tarps for various uses such as for covering structures and sheds, films for waterproofing, etc. Industrial bags, bags for packaging with greater mechanical resistance as well as against perforation and impact.Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C. Film obtained on a 50mm blow film line with barrier screw, 25:1 L/D, 1.0mm die gap, 50µm gauge, 2.3:1 BUR.Information provided by Dax Resinas
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ASTM D1505
Thickness 50.0 microns
1.97 mil
Melt Index of Compound 0.30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 380 %
380 %
ASTM D882
Film Elongation at Break, TD 765 %
765 %
ASTM D882
Secant Modulus, MD 0.120 GPa
17.4 ksi
5%; ASTM D882
Secant Modulus, TD 0.130 GPa
18.9 ksi
5%; ASTM D882
Coefficient of Friction, Dynamic 0.50
0.50
ASTM D1894
Elmendorf Tear Strength, MD 2.80 g/micron
71.1 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.60 g/micron
66.0 g/mil
ASTM D1922
Dart Drop Test 180 g
0.397 lb
(method A); ASTM D1709
Film Tensile Strength at Break, MD 31.0 MPa
4500 psi
ASTM D882
Film Tensile Strength at Break, TD 36.0 MPa
5220 psi
ASTM D882
Optical Properties Metric English Comments
Haze 16 %
16 %
ASTM D1003
Gloss 63 %
63 %
@ 60° Gardner; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 180 - 195 °C
356 - 383 °F
Plasticizing Zone
200 - 210 °C
392 - 410 °F
Mixture Zone
Feed Temperature 170 - 185 °C
338 - 365 °F
Adapter Temperature 210 - 225 °C
410 - 437 °F
Die Opening 0.0800 - 0.170 cm
0.0315 - 0.0669 in
Blow-up Ratio (BUR) 3.0
3.0
Recommended
Descriptive Properties Value Comments
Proportion LLDPE % 22.5
PTN-570-Q