Piezo Kinetics 700 Lead Zirconate Titanate Piezoelectric

Category	Ceramic , Oxide , Titanium Oxide , Zirconium Oxide , Piezoelectric
Manufacturer	Piezo Kinetics, Inc.
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Piezo Kinetics 700 Lead Zirconate Titanate Piezoelectric.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

This material has low dielectric constant, high QM, high shear coupling coefficient, good temperature stability and low aging characteristics. Common use of this material is in delay lines and accelerometers.Elastic Compliance s11E (x 10-12 m²/n): 10.8.Elastic Compliance s33E (x 10-12 m²/n): 13.9.Property data at 25°C. Information supplied by Piezo Kinetics, Inc.

Physical Properties	Metric	English	Comments
Density	7.60 g/cc	0.275 lb/in³

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	86.0 GPa	12500 ksi
Poissons Ratio	0.25	0.25
Shear Modulus	34.0 GPa	4930 ksi	calculated

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	150 °C	302 °F	Maximum Operating Temperature

Electrical Properties	Metric	English
Curie Temperature	350 °C	662 °F
Dielectric Constant	425 @Frequency 1000 Hz	425 @Frequency 1000 Hz
Dissipation Factor	0.015 @Frequency 1000 Hz	0.015 @Frequency 1000 Hz
Piezoelectric Longitudinal Coupling Factor, k33	0.66	0.66
Piezoelectric Transverse Voltage Coefficient, d31, 10^-12 m/V	-60.0	-60.0
Piezoelectric Shear Charge Coefficient, d15, 10^-12 m/V	362	362
Piezoelectric Longitudinal Voltage Coefficient, g33, 10^-3 V-m/N	39.9	39.9
Piezoelectric Planar Coupling Factor, kp	0.51	0.51
Piezoelectric Mechanical Q	600	600
Piezoelectric Shear Coupling Factor, k15	0.67	0.67
Piezoelectric Longitudinal Charge Coefficient, d33, 10^-12 m/V	150	150
Piezoelectric Transverse Voltage Coefficient, g31, 10^-3 V-m/N	-16.0	-16.0
Piezoelectric Shear Voltage Coefficient, g15, 10^-3 V-m/N	52	52
Piezoelectric Transverse Coupling Factor, k31	0.30	0.30