SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* KFL36 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| Flexural Strength | 123 MPa | 17800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.10 GPa | 1030 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.20 PHR Caytur 4
- Lucent Polymers GPP-240 Homopolymer Polypropylene, 40% Glass Fiber Reinforced, Chemically Coupled
- Techmer ES HiFill® PA6/6 GF/M40 L BK 40% Glass/Mineral Fiber Filled
- A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin
- Eagle Brass 510 Phosphor Bronzes 5% A, 1/2 Hard
- ChevronTexaco Delo® 2000 Marine Engine Oil, SAE 40
- Karina 02/223-G Yellow Color Concentrate for PVC
- Henkel Turco 5668 Paint Remover
- LG Chemical LUCON CP-4208F Conductive Thermoplastic, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved