- Samsung Cheil Industries Infino® AE-2130 PC/PET, Unreinforced
Samsung Cheil Industries Infino® AE-2130 PC/PET, Unreinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® AE-2130 PC/PET, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 260 °C |
21 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 81.4 MPa | 11800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.77 J/cm @Thickness 6.35 mm |
3.31 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 5.49 J/cm @Thickness 3.17 mm |
10.3 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 135 °C | 275 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID/L: 20-30/5-10 nm/0.5-2 um Short Multi-Walled Carbon Nanotubes
- SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer
- Lubrizol Advanced Materials Pearlthane® ECO 12T95 Thermoplastic Polyurethane
- Gwent Electronic Materials C2110127D3 Nanocopper based Paste
- Lanxess Durethan® BKV 30 G H2.0 900116 Nylon 6, 30% Glass Fiber
- Solvay ALKAMULS® OL 700 Surfactant
- ExxonMobil 3 Mobilith AW Series
- Lubrizol Stat-Rite® X5166 Static Dissipative Polystyrene Compound
- Murtfeldt Murpec® Polyetheretherketone
- Beijing Evergrow Resources PTFE, 24% Bronze, 12% Glass Fiber, 6% Graphite Filled
Copyright © lookpolymers.com All Rights Reserved