Samsung Cheil Industries Starex® GC-0710 ABS/PET, Unreinforced Recycled
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/Polyester Alloy , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® GC-0710 ABS/PET, Unreinforced Recycled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Eco-friendly Post-Consumer recycled PET.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D785 |
| Tensile Strength, Yield | 40.2 MPa | 5830 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 60.8 MPa | 8820 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.87 GPa | 272 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 6.35 mm |
2.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.75 J/cm @Thickness 3.17 mm |
5.14 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 6.40 mm |
176 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 94.0 °C | 201 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 25 % @Thickness 3.20 mm |
25 % @Thickness 0.126 in |
ASTM D1925 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 6 BT N 29 B PA6
- Polymer Resources NY6-G33-[color]-H Nylon 6, 33% Glass Reinforced, Heat Stabilized
- Mallard Creek Polymers Rovene® 8001 Hybrid Styrene-Butadiene Emulsion
- LG Chemical LUPOY HI-1002 High Impact Modified PC, Unreinforced
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 55-HR-1 TPE
- UBE UBEPOL BR230 Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- California Fine Wire Stablohm 650 Nickel Chromium Resistance Wire
- A. Schulman ComAlloy Comtuf® 106 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled, Impact Modified, UL
- Huntsman PE1451 EVA Film Extrusion (discontinued **)
- Ceradyne Ceralloy® 147-1E Silicon Nitride
Copyright © lookpolymers.com All Rights Reserved