- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Samsung Cheil Industries Starex® VG-4920F ABS, Glass Filled FR
Samsung Cheil Industries Starex® VG-4920F ABS, Glass Filled FR
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® VG-4920F ABS, Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 42 g/10 min @Load 10.0 kg, Temperature 220 °C |
42 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 85.3 MPa | 12400 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 5.88 GPa | 853 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 5.69 GPa | 825 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.17 mm |
1.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 0.598 J/cm @Thickness 6.35 mm |
1.12 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | B/50; ISO R306 |
| 102 °C | 216 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 1.60 - 3.00 mm |
V-0 @Thickness 0.0630 - 0.118 in |
|
| 5VB @Thickness 2.00 - 3.00 mm |
5VB @Thickness 0.0787 - 0.118 in |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible K85 Natural & Black Polyvinyl Chloride, Flexible (PVC, Flexible)
- Hexion Bakelite™ PF 1141 Phenolic Formaldehyde Resin, High Surface Quality, Resistant to High Temperatures, Dishwasher Proof
- Indium Corp. Indalloy 140 Bismuth Solder Alloy
- Greene Tweed CHEMRAZ® 543 Perfluoroelastomer
- Gwent Electronic Materials P2121112P5 Ammonia Plasma Modified Graphene Nanoplatelets
- Samsung Cheil Industries Infino® NH-1035 PC, Unreinforced FR
- Teknor Apex Monprene® MP-1277B Thermoplastic Elastomer
- Teknor Apex Telcar® TL-1000-95 Thermoplastic Elastomer
- A. Schulman POLYFORT™ FPP 3711 High Impact Polypropylene
- A. Schulman FORMION™ FI 389 Ionomer
Copyright © lookpolymers.com All Rights Reserved