- Samyang Triel® 5301SP Thermoplastics Polyetherester Elastomer, Double Extrusion
Samyang Triel® 5301SP Thermoplastics Polyetherester Elastomer, Double Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5301SP Thermoplastics Polyetherester Elastomer, Double Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5301SP is intended for double extrusion.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 - 0.017 cm/cm | 0.015 - 0.017 in/in | ASTM D955 |
| Melt Flow | 24 - 28 g/10 min @Load 2.16 kg, Temperature 230 °C |
24 - 28 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 30 | 30 | ASTM D2240 |
| Tensile Strength, Ultimate | 14.7 MPa | 2130 psi | ASTM D638 |
| Flexural Yield Strength | 2.26 MPa | 327 psi | ASTM D790 |
| Flexural Modulus | 0.0275 GPa | 3.98 ksi | ASTM D790 |
| Izod Impact, Notched | NB @Thickness 3.17 mm, Temperature -40.0 °C |
NB @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 3.17 mm, Temperature 23.0 °C |
NB @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 182 °C | 360 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXE154 PC
- LyondellBasell Petrothene® GA837091 Medium Density Polyethylene (Unverified Data**)
- Fujipoly Industries Sarcon® GR-Fk Gap Filler Pad
- Kuraray HYBRAR® F1 Foam Compound
- H.C. Starck Baymetec® Tungsten Silicide, WSi2
- Solvay Sulfuric Acid 98% Technical Grade
- Dow Corning C6-180 ELASTOMER KIT
- Ecomass® 1050ZD96 Tungsten Powder Filled Polyamide Alloy, Injection Molding Grade
- 3M 8421 Polyester Tape
Copyright © lookpolymers.com All Rights Reserved