Samyang Triel® 5552EM Thermoplastics Polyetherester Elastomer, Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5552EM Thermoplastics Polyetherester Elastomer, Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5552EM is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.017 - 0.020 cm/cm | 0.017 - 0.020 in/in | ASTM D955 |
| Melt Flow | 10 - 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 - 14 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Ultimate | 26.5 MPa | 3840 psi | ASTM D638 |
| Flexural Yield Strength | 9.32 MPa | 1350 psi | ASTM D790 |
| Flexural Modulus | 0.178 GPa | 25.7 ksi | ASTM D790 |
| Izod Impact, Notched | NB @Thickness 3.17 mm, Temperature -40.0 °C |
NB @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 3.17 mm, Temperature 23.0 °C |
NB @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 207 °C | 405 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ASTM D648 |
| Vicat Softening Point | 185 °C | 365 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL® 6370 Conductive Elastomer
- Fine Organics FINALUX G 732 Lubricant Additive
- Less Common Metals Terbium Sublimed Rare Earth Metal
- Kingfa PC-S609 Toughened PC
- Indium Corp. Indium Sulfamate Plating Bath
- Stir SpA C 2053 74 AT (PVC)
- DSM Novamid® 1017GH33 BK701 PA6-GF33
- Azoty Tarnow™ TARFLEN SM-1 PTFE
- Applied Composites 8038 Polyester SMC
- Chase Plastics CP Pryme® NN133GTL (DAM) Nylon 66, 33% Glass Fiber Reinforced, Toughened, Internally Lubricated
Copyright © lookpolymers.com All Rights Reserved