Solvay Specialty Polymers Halar® 930LCW Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE , ECTFE Fluoropolymer
Manufacturer Solvay Specialty Polymers
Trade Name Halar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Halar® 930LCW Ethylene Chlorotrifluoroethylene Copolymer (ECTFE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 °CInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ASTM D792
Water Absorption at Saturation <= 0.10 %
<= 0.10 %
ASTM D570
Linear Mold Shrinkage, Flow 0.025 cm/cm
0.025 in/in
Melt Flow 2.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 275 °C
2.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 527 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 90
90
ASTM D785
Hardness, Shore D 75
75
ASTM D2240
Tensile Strength at Break 54.0 MPa
7830 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 30.0 MPa
4350 psi
50 mm/min; ASTM D638
Elongation at Break 250 %
250 %
50 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ASTM D638
Tensile Modulus 1.66 GPa
241 ksi
50 mm/min; ASTM D638
Flexural Strength 47.0 MPa
6820 psi
2.5 mm/min; ASTM D790
Flexural Modulus 1.69 GPa
245 ksi
2.5 mm/min; ASTM D790
Izod Impact, Notched 2.10 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
3.93 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
ASTM D256
NB

@Thickness 3.20 mm,
Temperature 23.0 °C
NB

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Coefficient of Friction, Dynamic 0.20
0.20
vs. Itself; ASTM D1894
Coefficient of Friction, Static 0.30
0.30
vs. Itself; ASTM D1894
Taber Abrasion, mg/1000 Cycles 5.0
5.0
CS-17 Wheel, 500 g; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C
55.6 µin/in-°F
Specific Heat Capacity 0.962 J/g-°C
0.230 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.150 W/m-K

@Temperature 40.0 °C
1.04 BTU-in/hr-ft²-°F

@Temperature 104 °F
ASTM C177
Melting Point 242 °C
468 °F
DSC
Crystallization Temperature 222 °C
432 °F
Peak; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Unannealed; ASTM D648
Brittleness Temperature <= -76.0 °C
<= -105 °F
Procedure A; ASTM D746
Glass Transition Temp, Tg 85.0 °C
185 °F
ASTM E1356
Flammability, UL94 V-0
V-0
Oxygen Index 52 %
52 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 5.50e+16 ohm-cm
5.50e+16 ohm-cm
ASTM D257
Dielectric Constant 2.57

@Frequency 1.00e+6 Hz
2.57

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 14.0 kV/mm

@Thickness 3.18 mm
356 kV/in

@Thickness 0.125 in
ASTM D149
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Form Pellets
Processing Technique Extrusion