Polymer Property : Tensile Strength, Yield = 30.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	30.0 - 50.0 MPa	4350 - 7250 psi	Injection and Compression; ISO 527
Raschig Group EPOXIDUR® 3580 EP Epoxy Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This prod..
Tensile Strength, Yield	30.0 MPa	4350 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP CX05031 PS (Europe-Africa-Middle East) LNP* Lubricomp* CX05031 is a compound based on Polystyrene resin containing Graphite, Silicone. Added features include; Internally Lubricated.
Tensile Strength, Yield	30.0 MPa	4350 psi	2.0 in/min; 0.125" thickness; ASTM D-638
Chevron Phillips MA5350 HIPS - High Impact Polystyrene  (discontinued **) Rubber modified high impact polystyrene.Applications:Floppy diskettesDurable household applicationsThin to medium parts that require a combination of high gloss and good toughnessFeatures:Low coeffi..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
LyondellBasell Pro-fax 6329 Polypropylene Homopolymer, Improved Chemical Resistance Key Features: improved chemical resistance polypropylene homopolymer resin, FDA acceptable, easier processingApplications: closures, housewares, chairsMeets FDA requirements in 21 CFR 177.1520 for a..
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527
GEHR Plastics PP Polypropylene Polypropylene shows a high mechanical strength and a tensile strength, but a low notched impact strength. PP resists stress cracking and it is easy to weld. At minus temperatures it can get brittle...
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638-02
Ipiranga Petrochem GD 5160 HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
Tensile Strength, Yield	30.0 MPa <br>@Strain 0.200 %,<br> Temperature 1149 Â°C	4350 psi <br>@Strain 0.200 %,<br> Temperature 2100 Â°F
Haynes MultimetÂ® alloy, 1.6 mm thick sheet, 1177Â°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Tensile Strength, Yield	30.0 MPa <br>@Temperature 22.0 Â°C	4350 psi <br>@Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® BMC 2910 Unsaturated Polyester UP BMC 2910 incorporates additives which enhance the integral performance of mouldings during and after fire, currently used to mould Boltcaps which are designed to provide protection to the bolted co..
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527 type 1 A
Solvay TECHNYLÂ® C 442 Black V PA6, Conditioned Description: Unreinforced polyamide PA6, high viscosity, with high flexibility and very high impact resistance even at low temperature, for extrusion.Available in: Europe Product Applications: It ha..
Tensile Strength, Yield	30.0 MPa	4350 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers HalarÂ® 930LCW Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 Â°CInformation provided by Solvay Specialty Pol..
Tensile Strength, Yield	30.0 MPa	4350 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON AD000 ABS LNP* STAT-KON* AD000 is a compound based on ABS containing Carbon. Added feature of this grade is: Electrically Conductive.
Tensile Strength, Yield	30.0 MPa	4350 psi	50mm/min; ISO 527-2
Borealis Borclear™ RC707MO Polypropylene Borclear™ RC707MO is intended for blow molding. This grade provides high gloss, high transparency and excellent impact properties. This grade also features high heat distortion temperature. Applic..
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527-2
Borealis Daploy™ WB260HMS Polypropylene Daploy™ WB260HMS is a propylene-based, structurally isomeric polymer. Applications: cushioning and protective packaging, door liners, lightweight packaging trays, beakers and containers, microwave..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM-D638
Polyram RamOfin PPH313V4 Polypropylene, 20% Mineral Filled 20% mineral filled, impact modified polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527-2
Total PPH 9081 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 9081 is a controlled-rheology homopolymer. PPH 9081 is characterized by a narrow molecular weight distribution and excellent flow properties, providing improved impact res..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Total PPR 6523WZ Polypropylene, Nucleated Random Copolymer for Injection Molding Impact - 6523WZ produces molded parts with improved impact compared with parts molded from homopolymer polypropylene.Antistat - 6523WZ contains an antistat to help protect molded parts from dust acc..
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527-2
Total PS CPDS FT876 Flame Retardant Polystyrene POLYSTYRENE (PS) COMPOUND (CPDS) FT876 is a high impact, halogen free flame retardant polystyrene with good thermal stability and processability.Main Characteristics:Bromine and Chlorine free,UL94 V..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1068-32 Black40% Mineral Filled Polypropylene DescriptionPolyfort® FPP 1068-32 Black is a 40% mineral filled polypropylene designed for use when improved heat resistance, dimensional stability and high stiffness is needed. ApplicationApplicati..
Tensile Strength, Yield	30.0 MPa	4350 psi	Type 1 @ 2 in/min; ASTM D638
Chevron Phillips K-Resin® KR01 Styrene-Butadiene Copolymer, Injection Molding Grade Styrene-Butadiene CopolymerCustomer Benefits: This SBC can be processed by injection molding and extrusion into attractive useful parts that have excellent clarity, good toughness, good stiffness, h..
Tensile Strength, Yield	30.0 MPa	4350 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® L 20 W 20 grey 9280 PA12 Product Description: Grilamid L 20 W 20 grey 9280 is a semiflexible plasticized medium viscosity polyamide 12 (PA12) extrusion grade. Grilamid L 20 W 20 grey 9280 is heat stabilized. The main featur..
Tensile Strength, Yield	30.0 MPa	4350 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® L 20 W 20 PA12 Product Description: Grilamid L 20 W 20 is a semi-flexible plasticized medium viscosity polyamide 12 (PA12) extrusion grade. Grilamid L 20 W 20 is heat stabilized. The main features of Grilamid L 20..
Tensile Strength, Yield	30.0 MPa	4350 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® L 25 W 40 PA12 Product Description: Grilamid L 25 W 40 is a flexible, plasticised, high viscosity extrusion grade of Polyamide 12 (PA12) Grilamid L 25 W 40 is UV and heat stabilized. The main features of Grilamid ..
Tensile Strength, Yield	30.0 MPa	4350 psi	50 mm/min
Arkema Group Rilsan® AMN P30 LD Nylon 12, Flexible, Injection Grade (Dry) Designation ISO 1874-PA12-P,MLR,12-004Flexible grade for injection molding. Available color: black. Light stabilized. Mold-release agent.Good impact strength. Flexibility and dynamic properties. Eas..
Tensile Strength, Yield	30.0 MPa <br>@Temperature 80.0 °C	4350 psi <br>@Temperature 176 °F	ISO Data
BASF Ultramid® 8202 PA6 (Conditioned) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0339T40L Talc Reinforced
Tensile Strength, Yield	30.0 - 35.0 MPa	4350 - 5080 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 11008 PVDF Copolymer  (discontinued **) Key features of this grade: Low Viscosity, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVD..
Tensile Strength, Yield	30.0 MPa <br>@Strain 0.200 %,<br> Temperature 1204 °C	4350 psi <br>@Strain 0.200 %,<br> Temperature 2199 °F
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Tensile Strength, Yield	30.0 - 103 MPa	4350 - 15000 psi	Average value: 56.9 MPa Grade Count:15
Overview of materials for Polybutylene Terephthalate (PBT), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Mineral Filled". Each property range of values reported is minimum and..