Total Finathene® 6006 HDPE, blow molding, pipe (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total Finathene® 6006 HDPE, blow molding, pipe (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Finathene® 6006 is a high density polyethylene produced by the slurry loop low pressure polymerization process. Polymerization is conducted in the absence of any other comonomer. Finathene® 6006 has been especially developed for the manufacturing of small rigid bottles (up to 5 liters) for non aggressive solids and liquids. Its very low melt viscosity is particularly suitable for high output processing equipment. Finathene® 6006 is best processed at temperatures between 180 and 220°C.Information provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.

Physical Properties	Metric	English	Comments
Density	0.963 g/cc	0.0348 lb/in³	ISO 1183
Environmental Stress Crack Resistance	10 hour	10 hour	ASTM D1693-70
Melt Flow	0.65 g/10 min @Load 2.16 kg	0.65 g/10 min @Load 4.76 lb	ISO 1133
	3.0 g/10 min @Load 5.00 kg	3.0 g/10 min @Load 11.0 lb	ASTM D 1238
High Load Melt Index	50 g/10 min @Load 21.6 kg	50 g/10 min @Load 47.6 lb	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	21.0 MPa	3050 psi	ISO 527
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527
Elongation at Break	>= 700 %	>= 700 %	ISO 527
Elongation at Yield	8.0 %	8.0 %	ISO 527
Flexural Modulus	1.60 GPa	232 ksi	ISO 178
Tensile Impact Strength	50.0 kJ/m²	23.8 ft-lb/in²	Notched, -30°C; ISO 8256
	205 kJ/m²	97.5 ft-lb/in²	Notched, 23°C; ISO 8256

Thermal Properties	Metric	English	Comments
Vicat Softening Point	130 °C	266 °F	ISO 306

Descriptive Properties	Value	Comments
Food Approval	This material complies with the main regulations concerning non-toxicity of plastics materials in contact with food stuffs.