Unitika BV2120G15 PA66, 15% Glass Fiber Reinforced, Flame Retardant, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika BV2120G15 PA66, 15% Glass Fiber Reinforced, Flame Retardant, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 3.20 mm |
0.0080 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ISO 2039 |
| Tensile Strength at Break | 121 MPa | 17500 psi | ISO 527-1/-2 |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527-1/-2 |
| Tensile Modulus | 7.30 GPa | 1060 ksi | ISO 527-1/-2 |
| Flexural Strength | 169 MPa | 24500 psi | ISO 178 |
| Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.70 J/cm² | 17.6 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 223 °C | 433 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 28.0 kV/mm @Thickness 1.00 mm |
711 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Oceanchem Group 2,2-Dibromo-3-nitrilopropionamide (DBNPA)
- Quadrant EPP Quadrant PC 1000 Extruded, Unfilled, Polycarbonate (ASTM Product Data Sheet)
- Overview of materials for High Density Polyethylene (HDPE), Carbon Black Filled
- Momentive Performance Materials Siloprenâ„¢ LSR 2650 Liquid Silicone Rubber - Fast Cure / High Tear
- Multibase Multi-Flex® G 7150 TPE Styrene Ethylene Butylene Styrene Block Copolymer
- DuPont Elvax® 3165SB Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film
- DuPont Performance Polymers Delrin® PC650 NC010 Acetal (POM) (Unverified Data**)
- 3M AC-350 Class A-1 Aerospace Sealant
- DuPont Performance Polymers Zytel® 70G35HSRX BK099 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved