Zotefoams Plastazote® HD115 High Density Polyethylene Foam

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Zotefoams
Trade Name Plastazote®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® HD115 High Density Polyethylene Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0900 - 0.125 g/cc
0.00325 - 0.00452 lb/in³
sheet density
0.115 g/cc
0.00415 lb/in³
Nominal skin/skin; BS ISO 7214 1998
Cell Length 1.05 mm
0.0413 in
Typical Diameter
0.700 - 1.60 mm
0.0276 - 0.0630 in
Mechanical Properties Metric English Comments
Hardness, Shore OO 83
83
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 2.39 MPa
347 psi
ISO 7214 1998
Elongation at Break 95 %
95 %
Flexural Modulus 0.0230 GPa
3.34 ksi
BS4370, part 4, method 14
Compressive Yield Strength 0.667 MPa

@Strain 10.0 %
96.7 psi

@Strain 10.0 %
BS ISO 7214 1998
0.791 MPa

@Strain 25.0 %
115 psi

@Strain 25.0 %
BS ISO 7214 1998
0.805 MPa

@Strain 40.0 %
117 psi

@Strain 40.0 %
BS ISO 7214 1998
0.897 MPa

@Strain 50.0 %
130 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 8.31 kN/m
47.4 pli
BS EN ISO 8067 1995
Compression Set 7.0 %

@Time 79200 sec,
Strain 25.0 %
7.0 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
13.5 %

@Time 79200 sec,
Strain 25.0 %
13.5 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
14 %

@Time 79200 sec,
Strain 50.0 %
14 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
26 %

@Time 79200 sec,
Strain 50.0 %
26 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0769 W/m-K
0.534 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 130 °C
266 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 0.30

@Thickness 13.0 mm
0.30

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
0.50

@Thickness 5.00 mm
0.50

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998