Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | |
Plastcom SLOVAMID 6 T 10 PA6, mineral filling FeaturesDecreased shrinkage against the BT types, increased heat application up to 170°C. Increased modulus in tension - strength of the material. PA matrix reduction. Application eg. for tools, fi.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.010 cm/cm | 0.0075 - 0.010 in/in | ASTM D955 |
PolyOne Edgetek® AS-10GF/000 BLACK Acrylonitrile Butadiene Styrene (ABS) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
Lanxess Durethan® BKV 130 CS DUS008 600091 Nylon 6, 30% Glass Fiber PA 6, 30% glass fiber, injection molding, impact modifiedInformation provided by LANXESS. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.010 cm/cm | 0.0075 - 0.010 in/in | |
LATI Latamid 12 G/50 PA 12, 50% Glass Fiber Reinforced Polyamide 12 (PA12) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | |
LATI Latamid 66 LH2 G/35 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Oil stabilized. Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | |
LATI Laramid G/30 PPA, 30% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | |
LATI Latamid SP2 H2 G/35 PA 6.12, 35% Glass Fiber Reinforced, Heat Stabilized Polyamide 6.12 (PA6.12) based compound. Heat stabilized. Glass fibers. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provi.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0095 cm/cm | 0.0075 - 0.0095 in/in | |
LATI Latene® AG3H2W G/30-V0E PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Metal stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE freeAvailability: A.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | |
LATI Latene® AG7H2 G/50 PP Homopolymer, 50% Glass Fiber Reinforced, Heat Stabilized Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation prov.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | |
LATI Latilub 66-01M G/30 PA66, 30% Glass Fiber Reinforced, Molybdenum disulphide Filled Self-lubricating product based on Polyamide 66 (PA66). Molybdenum disulphide. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | |
LATI Latilub 82-05GR G/30 PA12, 30% Glass Fiber Reinforced, Graphite Filled Self-lubricating product based on Polyamide 12 (PA12). Graphite. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0090 cm/cm | 0.0075 - 0.0090 in/in | |
LATI Latishield 85-08A G/20 PES, Steel/Glass Fibers EMI shielding product based on Polyether Sulfone (PES). Steel fibers. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati .. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | |
Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, DRY Description: TECHNYL® A 218 V35 is a polyamide 66, reinforced with 35% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The .. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | GB/T 15585-1995 |
Sichuan Deyang Haton® hGR30 Polyphenylene Sulfide, Glass Fiber Reinforced Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0085 cm/cm @Time 86400 sec |
0.0075 - 0.0085 in/in @Time 24.0 hour |
ASTM D955 |
SABIC Innovative Plastics LNP THERMOCOMP LX08411 PEEK LNP* THERMOCOMP* LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added feature of this material is: Opaque. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | ISO DIS 294-4 |
Wellman Wellamid® GB1430-N 33% Glass Bubble Filled, Low Density Nylon 66 Description: Glass Bubble Filled, Low Density Nylon 66Information provided by Wellman. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0115 cm/cm | 0.0075 - 0.0115 in/in | ISO DIS 294-4 |
Wellman Wellamid® GFT15N050-BK2 15% Glass Fiber Toughened Nylon 66 Description: Glass Fiber Toughened Nylon 66Information provided by Wellman. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® 2665 MAS071 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® 3100 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® 3152 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® 3158 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® ET2613 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• Medium vi.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® ET3127 Polycarbonate Makrolon® polycarbonate resinMain characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characterist.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | Sheet |
BASF Ultradur B 4040 G10 BK5110 50% Glass Filled PBT Injection-molding grades containing 50% of glass fibers, for industrial parts with excellent surface quality.Applications: External door handles in vehicles, visible sunroof frames, over door handle.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | 60x60x2mm; ISO 294 |
BASF Ultradur S 4090 G6 30% Glass Filled PBT Ultradur S 4090 G6 is a 30% glass reinforced PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage.Applicati.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Thickness 2.00 mm |
0.0075 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
Covestro Makrolon® LQ2647 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Optical lens, safety g.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | LATI |
LATI LARAMID G/30 30% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**) Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | |
LATI Latiohm 75/4-03 PD01 G/20 PBT, 20% Glass Fiber Reinforced Semiconductive/dissipative product based on Polybutylene Terephthalate (PBT). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided.. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in | |
LATI Latiohm 75/4-08 PD01 G/30 PBT, 30% Glass Fiber Reinforced Semiconductive/dissipative product based on Polybutylene Terephthalate (PBT). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided.. |