Polymer Property : Linear Mold Shrinkage, Transverse = 0.0083 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.0083 cm/cm	0.0083 in/in
Plastcom SLOVAMID 6 GF 15 FRG 2 LW PA6, 15% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 15% glass fibre, with nonhalogen flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 960°..
Linear Mold Shrinkage, Transverse	0.0083 cm/cm @Thickness 3.00 mm	0.0083 in/in @Thickness 0.118 in	Mold Temp 80Â°C; Melt Temp 280Â°C; 400 bar; ISO 294-4
Lanxess DurethanÂ® BKV 215 H3.0 000000 Nylon 6-Copolymer, 15% Glass Fibers PA 6-Copolymer, 15% glass fibers, injection molding, impact modified
Linear Mold Shrinkage, Transverse	0.0083 cm/cm	0.0083 in/in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU (Asia Pacific) LNP* Lubricomp* GL003 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0083 cm/cm @Time 86400 sec	0.0083 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU (Asia Pacific) LNP* Lubricomp* GL003 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0083 cm/cm	0.0083 in/in	ISO 294-4
DSM Akulon® K224-G8 PA6-GF40 40% Glass Reinforced
Linear Mold Shrinkage, Transverse	0.0083 cm/cm	0.0083 in/in	60x60x2 mm; ISO 294
BASF Ultradur® S 4090 GX 14% Glass Filled PBT Description: Is a PBT + ASA, low-warpage, free-flowing injection-molding grades with very good processing capabilities, containing 14% of glass fibers for industrial parts with high dimensional stab..
Linear Mold Shrinkage, Transverse	0.0083 cm/cm	0.0083 in/in	ISO 294-4
Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..
Linear Mold Shrinkage, Transverse	0.0083 cm/cm @Time 86400 sec	0.0083 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP VERTON RX970079 PA 66 (Europe-Africa-Middle East) LNP* VERTON* RX970079 is a compound based on PA 66 resin containing Long Glass Fiber and PTFE. Added features include; Internally Lubricated.