SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU (Asia Pacific)
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* GL003 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0076 cm/cm | 0.0076 in/in | SABIC Method |
| 0.0076 cm/cm @Time 86400 sec |
0.0076 in/in @Time 24.0 hour |
ISO 294 | |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0083 cm/cm | 0.0083 in/in | SABIC Method |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 | |
| 0.0083 cm/cm @Time 86400 sec |
0.0083 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ASTM D638 |
| 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 | |
| 55.0 MPa | 7980 psi | ISO 527 | |
| 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 9.9 % | 9.9 % | ASTM D638 |
| 10 % | 10 % | Type I, 5 mm/min; ASTM D638 | |
| 11.8 % | 11.8 % | ISO 527 | |
| 11.8 % | 11.8 % | 5 mm/min; ISO 527 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| 79.0 MPa | 11500 psi | ISO 178 | |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | 2 mm/min; ISO 178 |
| 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D790 |
| 2.07 GPa | 300 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 2.30 GPa | 334 ksi | ISO 178 | |
| 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.91 J/cm | 16.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 54.0 kJ/m² | 25.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.23 | 0.23 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.12 | 0.12 | ASTM D3702 Modified |
| K (wear) Factor | 48.3 x 10-8 mm³/N-M | 24.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 169 °C | 336 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |