Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.30 - 0.65 g/10 min @Load 5.00 kg |
0.30 - 0.65 g/10 min @Load 11.0 lb |
±10% Superior Class, ±15% 1st Class |
Kazanorgsintez 271-274K Cable Composition Based on High Density Polyethylene Production Method: Gaseous-phase method. Application: Compositions are intended for cover insulating lapping, protective covers and cables.Information Provided by Kazanorgsintez |
|||
Melt Flow | 0.40 - 0.65 g/10 min | 0.40 - 0.65 g/10 min | ±10% Superior Class, ±18% 1st Class |
Kazanorgsintez 273-83 High Density Polyethylene Composite Production Method: Gaseous-phase method. Application: Composition of HD grade 273-83 is intended to obtain by method of extrusion products of industrial, cultural, and general use as well as goo.. |
|||
Melt Flow | 0.40 - 0.65 g/10 min | 0.40 - 0.65 g/10 min | ±10% Superior Class, ±18% 1st Class |
Kazanorgsintez 273-95 High Density Polyethylene Composite Production Method: Gaseous-phase method. Application: Composition of HD grade 273-95 is intended to obtain by method of extrusion products of industrial, cultural, and general use as well as goo.. |
|||
Melt Flow | 0.40 - 0.65 g/10 min | 0.40 - 0.65 g/10 min | ±18% |
Kazanorgsintez 296-83 High Density Polyethylene Composite Production Method: Compositions are achieved by ethylene copolymerization by gaseous-phase method at low pressure using complex catalysts on carrier material. Application: HDPE compositions 296-.. |