- Polymer Property : Melt Flow = 27 g/10 min
Polymer Property : Melt Flow = 27 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 27 g/10 min @Load 10.0 kg, Temperature 190 °C |
27 g/10 min @Load 22.0 lb, Temperature 374 °F |
ISO 1133 |
| Multibase TPSiV® 4200-70A Thermoplastic Elastomer FEATURES & BENEFITS: Soft silky feel; Excellent abrasion and scratch resistance; Excellent bonding to PC, ABS; Good chemical resistanceAPPLICATIONS: Solution for soft touch overmolding on consumer e.. |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polimeri Europa Flexirene® MS 40 U Linear Low Density Polyethylene Flexirene MS 40 U is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Parts made with Flexirene MS 40 U are characterized by a good balance be.. |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 230 °C |
27 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Dow INSPIRE™ D7030EZ Thermoplastic Polyolefin
(discontinued **) Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010, although this grade had previously been removed from Dow's standard product line. |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polimeri Europa Flexirene® MS 40 A Linear Low Density Polyethylene Flexirene MS 40 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Parts made with Flexirene MS 40 A are characterized by a good balance be.. |
|||
| Melt Flow | 27 - 37 g/10 min @Load 10.0 kg, Temperature 420 °C |
27 - 37 g/10 min @Load 22.0 lb, Temperature 788 °F |
ASTM D1238 |
| Mitsui AURUM® JCL3030 Polyimide, Carbon Fiber Filled
(discontinued **) AURUM JCL3030 is a high-performance polyimide for precision injection molded components and extruded products. A member of the AURUM family of advanced engineering resins, carbon fiber reinforced AU.. |
|||
| Melt Flow | 27 g/10 min @Load 5.00 kg, Temperature 300 °C |
27 g/10 min @Load 11.0 lb, Temperature 572 °F |
|
| Lehmann & Voss LUVOCOM® 50-1396 Polycarbonate, with carbon fiber, glass fiber and PTFE, electrically conducting Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
| Melt Flow | 27 g/10 min | 27 g/10 min | ASTM D1238 |
| Flint Hills P5M6K-080 Polypropylene Random Copolymer Features: Clarified, Gamma Radiation Sterilizable. Product does not contain animal derived components. Phthalate-free.Applications: Injection molding: Disposable Syringes. This product is not rec.. |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 240 °C |
27 g/10 min @Load 4.76 lb, Temperature 464 °F |
ASTM D1238 |
| LG Chemical KEYFLEX BT 1068D Ester Type TPE Description: Injection Molding, TPC-ET, General Purpose, High ModulusApplication: Injection Parts for Automotives, Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| LG Chemical LUCEL N127LD POM, Chemical Resistance Feature: Injection Molding, POM, Chemical ResistanceApplication: Copier, Watch, Clock, VCR, Printer Parts, etc.CAS No. 66455-31-0Information provided by LG Chemical |
|||
| Melt Flow | 27 g/10 min | 27 g/10 min | ASTM D1238 |
| Kolon Kocetal® K700 General Purpose Grade Acetal Copolymer Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ.. |
|||
| Melt Flow | 27 g/10 min @Load 10.0 kg, Temperature 220 °C |
27 g/10 min @Load 22.0 lb, Temperature 428 °F |
|
| KEP Kepital® F30 Acetal Copolymer Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| KEP Kepital® TX-31 Wear/Friction/Resistant Acetal Copolymer Kepital® is a registered trademark of Korea Engineering Plastics Co., Ltd. Information provided by Dayson Polymers. |
|||
| Melt Flow | 27 g/10 min @Load 10.0 kg, Temperature 220 °C |
27 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Ineos ABS Lustran® ABS 450 Injection Molding Grade Lustran® ABS 450 has medium impact strength, high flow, and is injection molding grade. |
|||
| Melt Flow | 27 g/10 min @Load 5.00 kg, Temperature 260 °C |
27 g/10 min @Load 11.0 lb, Temperature 500 °F |
Calculated from MVR using melt density; ISO 1133 |
| Lanxess Durethan® BC 40 SR2 000000 Nylon 6 PA 6 injection molding grade, high viscosity, non-reinforced, higher notched impact strength than BC 30, impact-modified |
|||
| Melt Flow | 27 g/10 min @Load 5.00 kg, Temperature 260 °C |
27 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Lanxess Durethan® BM 40 X H2.0 DUS009 901510 Nylon 6, 40% Glass Fiber + Mineral PA 6, injection molding grade, 40% glass fibers/mineral, good heat-ageing resistance |
|||
| Melt Flow | 27 g/10 min @Load 2.18 kg, Temperature 190 °C |
27 g/10 min @Load 4.80 lb, Temperature 374 °F |
ISO 1133 |
| Green Dot Terratek® Flex GDH-B1 Compostable Bioplastic Elastomer GDH-B1 is an elastomeric bioplastic with a diverse range of potential applications. It is a starch-based elastomer that is strong, durable and pliable with an exquisite soft touch. The bioplastic i.. |
|||
| Melt Flow | 27 g/10 min @Load 10.0 kg, Temperature 220 °C |
27 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Samsung Cheil Industries Infino® NH-1101 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | >= 27 g/10 min @Load 10.0 kg, Temperature 220 °C |
>= 27 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Styrolution Absolac® 920 ABS High flowMedium impactInformation provided by Styrolution |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 300 °C |
27 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D 1238 |
| SABIC Innovative Plastics LNP Thermocomp ZM3242 PPE+PS (Asia Pacific) Modified PPO* 30% mineral filled products, Non Halogenated Flame Retardant V-1 products.Supper low warpage series, HDT 110degCThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 230 °C |
27 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| SCG Chemicals EL-Proâ„¢ P740J Polypropylene Injection Molding Key Characteristics:Good flowabilityGood processabilityHigh stiffnessRecommended Applications:Automotive, motorcycle and electrical appliance parts that require good flowability such as automotive t.. |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 230 °C |
27 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Borealis HG455FB Polypropylene Homopolymer HG455FB is a polypropylene homopolymer intended for fiber applications. Applications: fine filament count at high spinning speeds, spun bonded nonwovens, and POY production.Information provided by .. |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 280 °C |
27 g/10 min @Load 4.76 lb, Temperature 536 °F |
JIS K 6719 |
| Zeon Chemicals Zeonor® 750R Cyclo Olefin Polymer Zeonor® is a line of thermoplastic polyolefin resin with an excellent combination of optical and electronic properties. These unique Cyclo Olefin Polymer (COP) was developed by Zeon Corporation usi.. |
|||
| Melt Flow | 27 g/10 min @Load 1.20 kg, Temperature 300 °C |
27 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
| Covestro Makrolon® DP 1-1456 Polycarbonate, Impact Grade Impact modified injection molding grade, extremely easy flow and easy mold release, for thin walled applications with long flow lengths.Information provided by Bayer.As of 1 September 2015, Bayer Ma.. |
|||
| Melt Flow | 27 g/10 min @Load 1.20 kg, Temperature 224 °C |
27 g/10 min @Load 2.65 lb, Temperature 435 °F |
ASTM D1238 |
| DSM Biomedical CarboSil® 20 90A Thermoplastic Silicone Polycarbonate Polyurethane (TSPCU) A ground-breaking copolymer that combines the biocompatibility and biostability of conventional silicone elastomers with the processability and toughness of thermoplastic polycarbonate-urethanes Th.. |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Dow ASPUN™ 6811A Linear Low-Density Polyethylene (LLDPE) ASPUN™ 6811A Fiber Grade Resin: Suggested Optimum Process: Spun Bond Typical Application: Non-woven FabricsInformation provided by Dow |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Azoty Tarnow™ TARNOFORM 500 POM Easy flowing grade for injection molding of thin-walled parts or in case of long flow path.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Barlog Plastics KEBAFORM C 270.0 POM Copolymer unreinforced POMInformation provided by BARLOG plastics GmbH. |
|||