Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 4.6 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.6 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
PolyOne Maxxam™ FR PP FR 7A11 Polypropylene, Unspecified (PP, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Melt Flow | 4.6 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.6 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
PolyOne Maxxam™ FR QD 818.Y001 Polypropylene, Unspecified (PP, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Melt Flow | 4.6 g/10 min @Load 6.60 kg, Temperature 337 °C |
4.6 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
SABIC Innovative Plastics ULTEM 3452 PEI 45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming, UL94 V0 and 5VA listing in recognized colors. |
|||
Melt Flow | 4.6 g/10 min @Load 6.60 kg, Temperature 337 °C |
4.6 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
SABIC Innovative Plastics ULTEM 3452 PEI (Asia Pacific) 45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming, UL94 V0 and 5VA listing in recognized colors. |
|||
Melt Flow | 4.6 g/10 min @Load 10.0 kg, Temperature 250 °C |
4.6 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL LEN2231 PPE+HIPS (Asia Pacific) PPE+PS Unfilled for LED Application |
|||
Melt Flow | 4.6 g/10 min @Load 2.16 kg, Temperature 235 °C |
4.6 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
UBE UBESTA® 3020GX6 Glass Fiber Reinforced Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: conductive, glass fiber reinforced, UV resistanceInformation provided by UBE. |
|||
Melt Flow | 4.6 g/10 min | 4.6 g/10 min | Conditions not specified; ASTM D1238 |
Total PPR 8473 Polypropylene, Film Extrusion Grade Random copolymer heat sealable film gradeColor/Clarity/Impact - FINA 8473 is a low melting, high ethylene random copolymer with improved color, optics and impact properties.Heat Sealable - The very .. |
|||
Melt Flow | 4.6 g/10 min @Load 5.00 kg, Temperature 260 °C |
4.6 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
Covestro Makroblend® DP 7665 Polycarbonate + PET, Mineral Filled Impact Grade Developmental productISO 7792-1-PC/PET,MHPR,-030,MD20(PC+PET)-blendsimpact modifiedInjection molding grade 20 % mineral filledPreprocessingMax. Water content |
|||
Melt Flow | 4.6 g/10 min @Load 2.16 kg, Temperature 235 °C |
4.6 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Conditioned) Designation ISO 1874-PA12,M,16-090,CF20Rigid grade with carbon fiber filler (20%) for injection molding. Available color: black. High strength-to-weight ratio. Very low shrinkage: include 0,5% on av.. |
|||
Melt Flow | 4.6 g/10 min @Load 2.16 kg, Temperature 235 °C |
4.6 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Dry) Designation ISO 1874-PA12,M,16-090,CF20Rigid grade with carbon fiber filler (20%) for injection molding. Available color: black. High strength-to-weight ratio. Very low shrinkage: include 0,5% on av.. |
|||
Melt Flow | 4.6 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.6 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
Arkema Group Altuglas® 84 L Acrylic-Styrene Copolymer ALTUGLAS 84 L is a new type of acrylic polymer produced by ATOHAAS which increases the range of material for injection molding applications. ALTUGLAS 84 L is a styrene methylmethacrylate copolymer s.. |
|||
Melt Flow | 4.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont™ Surlyn® 1652SB Zinc Ionomer Resin for Blown/Cast Film and Extrusion Coating Surlyn® 1652SB is an ionomer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylen.. |
|||
Melt Flow | 4.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Yparex 8104 E Polyolefin Adhesive Resin The Yparex range provides outstanding adhesion for all forms of polyethylene including cross-linked PE to: barrier plastics like EVOH and Polyamidemetals like aluminum, steel and copper.Yparex offer.. |