Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12,M,16-090,CF20Rigid grade with carbon fiber filler (20%) for injection molding. Available color: black. High strength-to-weight ratio. Very low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability (low moisture absorption). Antistatic properties.Example applications: Parts with high mechanical properties and dimensional precision.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
Melt Flow 4.6 g/10 min

@Load 2.16 kg,
Temperature 235 °C
4.6 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 132 MPa
19100 psi
5 mm/min
Elongation at Break 5.0 %
5.0 %
5 mm/min
Tensile Modulus 12.6 GPa
1830 ksi
1 mm/min
Charpy Impact Unnotched 5.90 J/cm²
28.1 ft-lb/in²
5.90 J/cm²

@Temperature -30.0 °C
28.1 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.70 J/cm²
8.09 ft-lb/in²
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
Melting Point 174 °C
345 °F
10°C/min
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in