Polymer Property : Melt Flow = 2.2 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	1.5 - 2.2 g/10 min @Load 5.00 kg, Temperature 190 °C	1.5 - 2.2 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
Polyplastic Torlen® PE 2K 901 High Density Polyethylene, Carbon Filled Information provided by PolyPlastic Group.
Melt Flow	1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 4116P (16402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Melt Flow	1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 4118N (18401) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Melt Flow	1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 5117P (18602) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Melt Flow	1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 5118P (18602) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Melt Flow	1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 4115P (16402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Melt Flow	1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 4117P (18402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Melt Flow	1.8 - 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 - 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 4118P (18402) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer