Polymer Property : Melt Index of Compound = 16 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer
High viscosity Proprietary Polycarbonate Ester, OSU 55/55 compliant, low smoke, flame retardant resin
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer (Asia Pacific)
High visocisty PC Copolymer, OSU 55/55 compliant, low smoke, flame retardant resin
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 300 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer (Europe-Africa-Middle East)
High viscosity PC Copolymer, OSU 55/55 compliant, low smoke, flame retardant resin
Melt Index of Compound 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® XHT1141 PC
XHT1141 is a high flow, high heat polycarbonate copolymer. It is the lowest heat product in the LEXAN* XHT portfolio. It is available in a range of opaque and limited transparent colors.
Melt Index of Compound 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® XHT1141 PC (Asia Pacific)
XHT1141 is a high flow, high heat polycarbonate copolymer. It is the lowest heat product in the LEXAN* XHT portfolio. It is available in a range of opaque and limited transparent colors.
Melt Index of Compound 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® XHT1141 PC (Europe-Africa-Middle East)
XHT1141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
Melt Index of Compound 16 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 16 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® 4022 PBT (Europe-Africa-Middle East)
VALOX 4022 is a 20% high strength glass fibre reinforced PBT injection moulding resin, with improved mechanical properties. Applications : Spotlights, appliance housings and handles.
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® 771 PBT (Europe-Africa-Middle East)
VALOX 771 is a 15% glass and 20% mineral filled, flame retarded injection moulding PBT resin.
Melt Index of Compound 16 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 16 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® V8030CS PBT+PET
Glass filled Valox with enhanced surface
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® IQ357M PBT+PC (Europe-Africa-Middle East)
Valox* Resin IQ357M: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified, easy flow product with mold release.
Melt Index of Compound 16 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 16 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® SHF4930 PBT (Europe-Africa-Middle East)
Super high flow FR PBT grade with 15% Glass reinforced