Polymer Property : Tensile Strength = 23900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	165 MPa	23900 psi	ASTM D638
NHEP Spectron™ E5469 Nylon 66, 33% Glass Fiber Natural color. E5469 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informat..
Tensile Strength	165 MPa	23900 psi	ASTM D638
NHEP Spectron™ E6666 Nylon 66, 30% Glass Fiber Natural color. E6666 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informati..
Tensile Strength	165 MPa	23900 psi	ASTM D638
PolyOne Bergamid™ XP6042701 Polyamide 6 (Nylon 6) Injection Speed: 50 to 80% Holding Time: 3 to 9 sec Injection Time: 1 to 3.5 sec Cycle Time: 18 to 60 secInformation provided by PolyOne
Tensile Strength	165 MPa @Temperature 23.0 °C	23900 psi @Temperature 73.4 °F	DAM; ASTM D638
DuPont Performance Polymers Zytel® 77G33L BK031 Nylon 612 (Unverified Data**) Zytel® 77G33L BK031 is a 33% glass fiber reinforced, black polyamide 612 resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength	165 MPa	23900 psi	ASTM D638
Kuraray Genestarâ„¢ G1302 Nylon, 30% Glass Filled Abrasion Resistance HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. It delivers low..
Tensile Strength	165 MPa	23900 psi	ASTM D638
Kuraray Genestarâ„¢ GN2332 Nylon, 33% Glass Filled High Flow V-0 Grade. Improves flow-ability in thin-walled parts. Used for components requiring high-flowability, such as 0.3 mm pitch connectors.
Tensile Strength	165 MPa	23900 psi	ASTM D638
Kuraray Genestarâ„¢ GP2450NH-2 Nylon, 45% Glass Filled Standard V-0 Grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.This grade meets UL94, V-0..
Tensile Strength	165 MPa	23900 psi	ASTM D638
Kuraray Genestarâ„¢ GW2458HF Nylon, 45% Glass Filled Low Warpage, High Flow V-0 Grade. It is suited for low warpage and high flow applications, making it well suited for card connectors.
Tensile Strength	165 MPa	23900 psi	ASTM D638
Solvay Specialty Polymers RytonÂ® R-4-230BL Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4-230NA and R-4-230BL 40% glass fiber reinforced polyphenylene sulfide compounds provide reduced flash and improved processability compared to other polyphenylene sulfide injection moldi..
Tensile Strength	165 MPa	23900 psi	ASTM D638
Solvay Specialty Polymers RytonÂ® R-4-240BL Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4-240NA and R-4-240BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and toughness compared to other polyphenylene sulfide compounds.Feat..
Tensile Strength	165 MPa	23900 psi	dry; ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF40 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 40% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning..
Tensile Strength	165 MPa	23900 psi	Alloy 1100 Property; ASTM D345
Arlon 91B32R016AC Aluminum Clad Silicone Press Pad with "C-finish" Design/Construction:Side 2: Alloy 1100 H18 Aluminum FoilSide 1: Cured Silicone RubberThis data represents typical values for the production material and should not be used as material specificatio..