DuPont Performance Polymers Zytel® 77G33L BK031 Nylon 612 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® 77G33L BK031 Nylon 612
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® 77G33L BK031 is a 33% glass fiber reinforced, black polyamide 612 resin for injection molding.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | DAM; ASTM D792 |
| Density | 1.32 g/cc | 0.0477 lb/in³ | DAM; ISO 1183 |
| Filler Content | 33 % | 33 % | DAM |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 1.60 mm |
0.0010 in/in @Thickness 0.0630 in |
Flow; DAM |
| 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
Flow; DAM | |
| 0.0040 cm/cm @Thickness 6.40 mm |
0.0040 in/in @Thickness 0.252 in |
Flow; DAM | |
| 0.0090 cm/cm @Thickness 1.60 mm |
0.0090 in/in @Thickness 0.0630 in |
Transverse; DAM | |
| 0.010 cm/cm @Thickness 3.20 mm |
0.010 in/in @Thickness 0.126 in |
Transverse; DAM | |
| 0.011 cm/cm @Thickness 6.40 mm |
0.011 in/in @Thickness 0.252 in |
Transverse; DAM | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm |
0.0030 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm |
0.0090 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa @Temperature 23.0 °C |
20300 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 168 MPa @Temperature 23.0 °C |
24400 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Tensile Strength | 165 MPa @Temperature 23.0 °C |
23900 psi @Temperature 73.4 °F |
DAM; ASTM D638 |
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
DAM; ASTM D638 |
| 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
DAM; ISO 527 | |
| 3.2 % @Temperature 23.0 °C |
3.2 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 7.90 GPa @Temperature 23.0 °C |
1150 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 9.50 GPa @Temperature 23.0 °C |
1380 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Flexural Strength | 245 MPa @Temperature 23.0 °C |
35500 psi @Temperature 73.4 °F |
DAM; ASTM D790 |
| Flexural Modulus | 8.20 GPa @Temperature 23.0 °C |
1190 ksi @Temperature 73.4 °F |
DAM; ASTM D790 |
| 8.20 GPa @Temperature 23.0 °C |
1190 ksi @Temperature 73.4 °F |
DAM; ISO 178 | |
| Izod Impact, Notched | 1.06 J/cm @Temperature 23.0 °C |
1.99 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 |
| Izod Impact, Unnotched | 10.65 J/cm @Temperature 23.0 °C |
19.95 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -40.0 °C |
5.23 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A |
| 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 | |
| 500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
DAM; ASTM E 831 | |
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
46.1 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 |
| 83.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
46.1 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |
| 113 µm/m-°C @Temperature 23.0 - 55.0 °C |
62.8 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 | |
| 113 µm/m-°C @Temperature 23.0 - 55.0 °C |
62.8 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| 158 µm/m-°C @Temperature 55.0 - 160 °C |
87.8 µin/in-°F @Temperature 131 - 320 °F |
DAM; ASTM E 831 | |
| 158 µm/m-°C @Temperature 55.0 - 160 °C |
87.8 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |
| Melting Point | 215 °C | 419 °F | DAM; ASTM D3418 |
| 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | DAM; ASTM D648 |
| 200 °C | 392 °F | DAM; ISO 75-1/-2 | |
| UL RTI, Electrical | 105 °C @Thickness 0.710 mm |
221 °F @Thickness 0.0280 in |
DAM; UL 746B |
| 120 °C @Thickness 1.50 mm |
248 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 120 °C @Thickness 3.00 mm |
248 °F @Thickness 0.118 in |
DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 120 °C @Thickness 1.50 mm |
248 °F @Thickness 0.0591 in |
DAM; UL 746B |
| 120 °C @Thickness 3.00 mm |
248 °F @Thickness 0.118 in |
DAM; UL 746B | |
| Flammability, UL94 | HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
DAM; IEC 60695-11-10 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; UL94 | |
| HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
DAM; UL94 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; UL94 | |
| Glow Wire Test | 675 °C @Thickness 1.50 mm |
1250 °F @Thickness 0.0591 in |
DAM; IEC 60695-2-12 |
| 675 °C @Thickness 0.710 mm |
1250 °F @Thickness 0.0280 in |
DAM; IEC 60695-2-12 | |
| 700 °C @Thickness 3.00 mm |
1290 °F @Thickness 0.118 in |
DAM; IEC 60695-2-12 | |
| 700 °C @Thickness 0.710 mm |
1290 °F @Thickness 0.0280 in |
DAM; Ignition; IEC 60695-2-13 | |
| 700 °C @Thickness 1.50 mm |
1290 °F @Thickness 0.0591 in |
DAM; Ignition; IEC 60695-2-13 | |
| 725 °C @Thickness 3.00 mm |
1340 °F @Thickness 0.118 in |
DAM; Ignition; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V @Temperature 23.0 °C |
600 V @Temperature 73.4 °F |
DAM; UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum |
| 280 - 300 °C | 536 - 572 °F | DAM | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
Users viewing this material also viewed the following:
- Northstar Polymers PPF-028 Curing Agent
- PlastiComp Complet® LCF20/LGF20 – PA66 BLK Polyamide 66, 40% Long Carbon/Glass Fiber
- Mitsui AURUM® JGN6230 Thermoplastic Polyimide Resin, Amorphous (discontinued **)
- Lord Adhesives Flocklok® Catalyst 1
- Lotte Chemical Titan TITANPRO® PM383 Polypropylene homopolymer
- Special Metals INCONEL® C276 Nickel Superalloy Tubing, 30% Cold Work
- Polyplastics Duracon® M450-44/M450S Acetal Co-polymer (POM), Standard, Super high flow, High cycle
- CP-Polymer-Technik Wellamid® 6600/42 HWCP Nylon 66, Polymer Modified, Heat Stabilized, Dry
- SABIC Innovative Plastics ULTEM 1000E PEI
- Gouda Vuurvast ADHESIET 170 P Dry Air-Setting Refractory Mortar
Copyright © lookpolymers.com All Rights Reserved