Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 29.0 MPa | 4200 psi | ASTM D412 |
Northstar Polymers MSS-A70GQ High Performance Polyurethane Cast Elastomer System 70A This is a Ester/MDI base high-performance polyurethane casting system. This systems is recommended to applications in which the part requires cut/tear resistance, dry-abrasion resistance, slow resp.. |
|||
Tensile Strength | 29.0 MPa | 4200 psi | ASTM D412 |
Northstar Polymers MSS-A90A High Performance Polyurethane Cast Elastomer System 90A This is a Ester/MDI base high-performance polyurethane casting system. This systems is recommended to applications in which the part requires high tensile strength, cut/tear resistance, dry-abrasio.. |
|||
Tensile Strength | 29.0 MPa | 4200 psi | 2 in/min; ASTM D638 |
Braskem TI4003F Impact Copolymer Polypropylene Description: Extra High Izod Impact, Very High Flexural Modulus, Good Low Temperature Drop ImpactApplications: Suggested Uses Include Blow Molding, Extrusion, Profiles, PipeThis resin meets the requ.. |
|||
Tensile Strength | 29.0 MPa | 4200 psi | 2 in/min; ASTM D638 |
Braskem TI4005F Impact copolymer Polypropylene Description: Extra high izod impact, very high flexural modulus, good low temperature drop impact.Applications: Suggested uses include compounding and thermoforming.Process: Thermoforming.This resin.. |
|||
Tensile Strength | 29.0 MPa | 4200 psi | 2 in/min; ASTM D638 |
Braskem TI4007G Impact Copolymer Polypropylene Description: Extra high izod impact, superior low temperature drop impact.Applications: Suggested uses include profiles, tubing, squeeze bottles. UL temperature index of 100ºC.Process: Injection Mo.. |
|||
Tensile Strength | 29.0 MPa | 4200 psi | 2 in/min; ASTM D638 |
Braskem TR3020F Random Copolymer Polypropylene Description: High flexural modulus. Applications: Suggested uses include extrusion, blow molding. Process: Extrusion. This resin meets the requirements for olefin polymers as defined in 21 CFR, se.. |
|||
Tensile Strength | 29.0 MPa | 4200 psi | ASTM D638 |
Aaron Industries AAROPRENE® TFIPP 2020 High Impact Talc Filled Polypropylene AAROPRENE® TFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
Tensile Strength | 29.0 MPa | 4200 psi | ASTM D638 |
Aaron Industries AAROPRENE® TFPP 2010 Talc Filled Polypropylene AAROPRENE® TFPP 2000 Series Talc Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
Tensile Strength | 29.0 MPa | 4200 psi | ASTM D638 |
Aaron Industries AAROPRENE® CFPP 2020 Calcium Carbonate Filled Polypropylene AAROPRENE® CFPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
Tensile Strength | 28.9 MPa | 4200 psi | ASTM D638 |
Samyang Trilen® 9550T30 Polypropylene, Reinforced Mechanical strength and thermal resistance are excellent.9550T30 is a non-flame retardant, reinforced grade.Information provided by Samyang. |