Polymer Property : Compressive Strength = 1.20 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	1.20 MPa	174 psi	perpendicular to plane; ASTM D1621
SABIC Innovative Plastics ULTEM Foam XP080 PEI ULTEM foam is a polyetherimide based thermoplastic foam with excellent flame, smoke and toxicity performance. The material combines a high strength to weight ratio with low moisture absorption. The ..
Compressive Strength	1.20 MPa	174 psi	perpendicular to plane; ASTM D1621
SABIC Innovative Plastics ULTEM Foam XP080 PEI (Asia Pacific) ULTEM foam is a polyetherimide based thermoplastic foam with excellent flame, smoke and toxicity performance. The material combines a high strength to weight ratio with low moisture absorption. The ..
Compressive Strength	>= 1.20 MPa	>= 174 psi	@ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621
Samsung Cheil Industries StarexÂ® SF-400H Expandable Polystyrene (EPS) FR Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries.
Compressive Strength	>= 1.20 MPa	>= 174 psi	@ 25 kg/m<sup>2</sup>; JIS A9511, ASTM D1621
Samsung Cheil Industries StarexÂ® SG-501 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries.
Compressive Strength	>= 1.20 MPa	>= 174 psi	@ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621
Samsung Cheil Industries StarexÂ® SF-400H Expandable Polystyrene (EPS) FR Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries.
Compressive Strength	>= 1.20 MPa	>= 174 psi	@ 25 kg/m<sup>2</sup>; JIS A9511, ASTM D1621
Samsung Cheil Industries StarexÂ® SG-501 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries.
Compressive Strength	1.20 MPa	174 psi	In the Foaming Direction
Cymat A35620SC 020SS Stabilized Aluminum Foam Description: Cymat A35620SC 020SS stabilized aluminum foam (SAF) is a closed cell aluminum foam formed from A356 aluminum alloy with a density of 0.2 g/cm3. The mechanical properties of SAF make it ..
Compressive Strength	>= 1.20 MPa	>= 174 psi	perpendicular to plane; ISO 844
3A Composites Core Materials AIREX® T92.100 Easy Processing Structural Foam AIREX® T92 is a closed-cell, thermoplastic and recyclable polymer foam with very good mechanical properties and price / performance ratio. It has a good resistance to fatigue, is chemically stable,..
Compressive Strength	>= 1.20 MPa	>= 174 psi	perpendicular to plane; ISO 844
3A Composites Core Materials AIREX® R82.110 High Performance Structural Foam AIREX® R82 is a closed-cell, thermoplastic polymer foam that combines outstanding fire resistance with low smoke and toxicity, along with excellent dielectric properties. It has a good strength to ..
Compressive Strength	>= 1.20 MPa	>= 174 psi	perpendicular to plane; ISO 844
3A Composites Core Materials AIREX® T90.100 Easy Processing Structural FST Foam AIREX® T90 is a closed-cell, thermoplastic and recyclable polymer foam with excellent fire, smoke & toxicity (FST) properties. It has very good mechanical properties and a good resistance to fatigu..