Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 1.20 MPa | 174 psi | perpendicular to plane; ASTM D1621 |
SABIC Innovative Plastics ULTEM Foam XP080 PEI ULTEM foam is a polyetherimide based thermoplastic foam with excellent flame, smoke and toxicity performance. The material combines a high strength to weight ratio with low moisture absorption. The .. |
|||
Compressive Strength | 1.20 MPa | 174 psi | perpendicular to plane; ASTM D1621 |
SABIC Innovative Plastics ULTEM Foam XP080 PEI (Asia Pacific) ULTEM foam is a polyetherimide based thermoplastic foam with excellent flame, smoke and toxicity performance. The material combines a high strength to weight ratio with low moisture absorption. The .. |
|||
Compressive Strength | >= 1.20 MPa | >= 174 psi | @ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SF-400H Expandable Polystyrene (EPS) FR Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 1.20 MPa | >= 174 psi | @ 25 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-501 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 1.20 MPa | >= 174 psi | @ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SF-400H Expandable Polystyrene (EPS) FR Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 1.20 MPa | >= 174 psi | @ 25 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-501 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | 1.20 MPa | 174 psi | In the Foaming Direction |
Cymat A35620SC 020SS Stabilized Aluminum Foam Description: Cymat A35620SC 020SS stabilized aluminum foam (SAF) is a closed cell aluminum foam formed from A356 aluminum alloy with a density of 0.2 g/cm3. The mechanical properties of SAF make it .. |
|||
Compressive Strength | >= 1.20 MPa | >= 174 psi | perpendicular to plane; ISO 844 |
3A Composites Core Materials AIREX® T92.100 Easy Processing Structural Foam AIREX® T92 is a closed-cell, thermoplastic and recyclable polymer foam with very good mechanical properties and price / performance ratio. It has a good resistance to fatigue, is chemically stable,.. |
|||
Compressive Strength | >= 1.20 MPa | >= 174 psi | perpendicular to plane; ISO 844 |
3A Composites Core Materials AIREX® R82.110 High Performance Structural Foam AIREX® R82 is a closed-cell, thermoplastic polymer foam that combines outstanding fire resistance with low smoke and toxicity, along with excellent dielectric properties. It has a good strength to .. |
|||
Compressive Strength | >= 1.20 MPa | >= 174 psi | perpendicular to plane; ISO 844 |
3A Composites Core Materials AIREX® T90.100 Easy Processing Structural FST Foam AIREX® T90 is a closed-cell, thermoplastic and recyclable polymer foam with excellent fire, smoke & toxicity (FST) properties. It has very good mechanical properties and a good resistance to fatigu.. |