Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | Average value: 2200 MPa Grade Count:12 |
Overview of materials for Polycarbonate, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Extruded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Tensile Creep Modulus, 1 hour | 2200 - 10100 MPa | 319000 - 1.46e+6 psi | Average value: 5970 MPa Grade Count:3 |
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Lanxess Pocan® B 1501 000000 PBT PBT, non-reinforced, injection molding, extrusion, food contact |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 1804 Polycarbonate MVR (300 °C/1.2 kg) 6.0 cm3/10 minhigh viscosityUV stabilizedoptimized for low plate-outimproved flammabilityUL 94 V-2/1.5 mm and 3.0 mmavailable in transparenttranslucent and opaque colorssolid sh.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 1952 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardancy• Me.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 2256 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 2405 MAS048 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® 2405 Polycarbonate, Injection Grade Very easy flowing injection molding grade with easy mold release, Makrolon grade 2458 for food contact applications.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was se.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 2408 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 2600 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 2665 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medium viscosity, easy.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 2667 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® 2807 Polycarbonate, Injection Grade Medium flowing injection molding grade with easy mold release and UV stabilizer.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 2865 Polycarbonate, Flame Retardant Grade ISO 7391-PC,MFR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 9.5 cm3/10 minChlorine- and bromine-free flame retardantUL 94V-2/1.5 mm and 3.0 mmMedium viscosityEasy releaseInjection molding - Melt tempe.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 3103 MAS157 Polycarbonate ISO 7391-PC,EL,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minExtrusionHigh viscosityUV stabilizedAvailable in color code 550115 onlySolid sheetCorrugated sheetPreprocessingMax. Water conte.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® 3107 Polycarbonate ISO 7391-PC,MLR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minGeneral purposeHigh viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in transpare.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® 3158 Polycarbonate Key Features:Release agentUnfilledSuitable processing methods:Injection moldingExtrusionBlow moldingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® 3208 Polycarbonate Injection molding and extrusion grade with high viscosity, BgVV- and FDA grade for food contact applications, yields especially tough parts, better resistance to hot water.Information provided by Ba.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® 6385 Polycarbonate, Injection Grade Low viscosity, flame retardant injection molding grade with easy mold release, not available in transparent colors.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was sep.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® 6485 Polycarbonate, Injection Grade Medium viscosity, flame retardant injection molding grade with easy mold release, not available in transparent colors.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was .. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® 6555 Polycarbonate, Injection Grade Medium viscosity, flame retardant injection molding with easy mold release, burning behavior.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG a.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® 6557 Polycarbonate, Injection Grade Medium viscosity, flame retardant injection molding grade with easy mold release, UV-stabilized.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer A.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® FU4007 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Furniture applications.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® LQ 2647 Polycarbonate, UV-Stabilized UV-stabilized injection molding grade with easy mold release, suitable for spectacle glasses (LQ = Lens Quality).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separ.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® DP1-1843* Polycarbonate ISO 7391-PC,RL,(,,)-09-9Developmental productMVR (300 °C/1.2 kg) 9.5 cm3/10 minMedium viscosityUV stabilizedRotomoldingAvailable in transparent and translucent colorsGlobe lightsAs of 1 September 2.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® ET2613 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• Medium vi.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® ET3227 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• High visc.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® KU 1-1216 Polycarbonate, UV-Stabilized UV-stabilized injection molding grade, good flow, suitable for spectacle glasses (LQ = Lens-Quality).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Ba.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
Covestro Makrolon® LQ3187 Polycarbonate ISO 7391-PC,MLR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minOptical lensHigh viscosityUV stabilizedUV 400 cut offEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable i.. |
|||
Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
Covestro Makrolon® LQ 2643 Polycarbonate, UV-Stabilized UV-stabilized injection molding grade, good flow, suitable for spectacle glasses (LQ = Lens-Quality).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Ba.. |