Covestro Makrolon® 2405 MAS048 Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Covestro
Trade Name Makrolon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Makrolon® 2405 MAS048 Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low viscosity, easy releaseAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Bulk Density 0.660 g/cc
0.0238 lb/in³
pellets; ISO 60
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183-1
Moisture Absorption at Equilibrium 0.12 %
0.12 %
ISO 62, 50% RH
Water Absorption at Saturation 0.30 %
0.30 %
ISO 62
Water Vapor Transmission 15.0 g/m²/day

@Thickness 0.100 mm
0.966 g/100 in²/day

@Thickness 0.00394 in
85% RH, film; ISO 15106-1
Oxygen Transmission 80.0 cc-mm/m²-24hr-atm

@Thickness 0.0254 mm
203 cc-mil/100 in²-24hr-atm

@Thickness 0.00100 in
3150 cc/m²-24hr-bar; film; b.o. ISO 2556
80.0 cc-mm/m²-24hr-atm

@Thickness 0.100 mm
203 cc-mil/100 in²-24hr-atm

@Thickness 0.00394 in
800 cc/m²-24hr-bar; film; b.o. ISO 2556
Nitrogen Transmission 16.0 cc-mm/m²-24hr-atm

@Thickness 0.100 mm
40.6 cc-mil/100 in²-24hr-atm

@Thickness 0.00394 in
160 cc/m²-24hr-bar; film; b.o. ISO 2556
16.0 cc-mm/m²-24hr-atm

@Thickness 0.0254 mm
40.6 cc-mil/100 in²-24hr-atm

@Thickness 0.00100 in
630 cc/m²-24hr-bar; film; b.o. ISO 2556
Carbon Dioxide Transmission 480 cc-mm/m²-24hr-atm

@Thickness 0.0254 mm
1220 cc-mil/100 in²-24hr-atm

@Thickness 0.00100 in
18900 cc/m²-24hr-bar; film; b.o. ISO 2556
480 cc-mm/m²-24hr-atm

@Thickness 0.100 mm
1220 cc-mil/100 in²-24hr-atm

@Thickness 0.00394 in
4800 cc/m²-24hr-bar; film; b.o. ISO 2556
Linear Mold Shrinkage, Flow 0.0065 cm/cm

@Thickness 2.00 mm
0.0065 in/in

@Thickness 0.0787 in
60x60x2 mm; 500 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0065 cm/cm

@Thickness 2.00 mm
0.0065 in/in

@Thickness 0.0787 in
60x60x2 mm; 500 bar; ISO 294-4
Melt Flow 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Mechanical Properties Metric English Comments
Puncture Resistance 5100 N

@Temperature 23.0 °C
1150 lb (f)

@Temperature 73.4 °F
ISO 6603-2
6000 N

@Temperature -30.0 °C
1350 lb (f)

@Temperature -22.0 °F
ISO 6603-2
Ball Indentation Hardness 115 MPa
16700 psi
ISO 2039-1
Tensile Strength at Break 65.0 MPa
9430 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 50 %
>= 50 %
Nominal, 50 mm/min; ISO 527-1,-2
120 %
120 %
50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 97.0 MPa
14100 psi
2 mm/min; ISO 178
Flexural Yield Strength 73.0 MPa

@Strain 3.50 %
10600 psi

@Strain 3.50 %
2 mm/min; ISO 178
Flexural Modulus 2.35 GPa
341 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Thickness 3.20 mm,
Temperature -30.0 °C
5.71 ft-lb/in²

@Thickness 0.126 in,
Temperature -22.0 °F
complete break; b.o. ISO 180-A
75.0 kJ/m²

@Thickness 3.20 mm,
Temperature 23.0 °C
35.7 ft-lb/in²

@Thickness 0.126 in,
Temperature 73.4 °F
partial break; b.o. ISO 180-A
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179-1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179-1eU
NB

@Temperature -60.0 °C
NB

@Temperature -76.0 °F
ISO 179-1eU
Charpy Impact, Notched 1.40 J/cm²

@Thickness 3.00 mm,
Temperature -30.0 °C
6.66 ft-lb/in²

@Thickness 0.118 in,
Temperature -22.0 °F
complete break; ISO 7391/b.o. ISO 179-1eA
6.50 J/cm²

@Thickness 3.00 mm,
Temperature 23.0 °C
30.9 ft-lb/in²

@Thickness 0.118 in,
Temperature 73.4 °F
partial break; ISO 7391/b.o. ISO 179-1eA
Puncture Energy 55.0 J

@Temperature 23.0 °C
40.6 ft-lb

@Temperature 73.4 °F
ISO 6603-2
65.0 J

@Temperature -30.0 °C
47.9 ft-lb

@Temperature -22.0 °F
ISO 6603-2
Tensile Creep Modulus, 1 hour 2200 MPa
319000 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 1900 MPa
276000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 65.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
36.1 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 65.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
36.1 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
cross-flow; ISO 8302
Hot Ball Pressure Test 136 °C
277 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 137 °C
279 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
ISO 75-1,-2
Vicat Softening Point 145 °C

@Load 5.10 kg
293 °F

@Load 11.2 lb
50°C/h; ISO 306
146 °C

@Load 5.10 kg
295 °F

@Load 11.2 lb
120°C/h; ISO 306
Glass Transition Temp, Tg 145 °C
293 °F
10°C/min; ISO 11357-1,-2
Flammability, UL94 HB

@Thickness 2.70 mm
HB

@Thickness 0.106 in
V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
Flash Point 480 °C
896 °F
ASTM D 1929
550 °C
1020 °F
self ignition; ASTM D 1929
Oxygen Index 27 %
27 %
Method A; ISO 4589-2
Glow Wire Test 850 °C

@Thickness 1.00 mm
1560 °F

@Thickness 0.0394 in
GWFI; IEC 60695-2-12
850 °C

@Thickness 1.50 mm
1560 °F

@Thickness 0.0591 in
GWFI; IEC 60695-2-12
850 °C

@Thickness 2.00 mm
1560 °F

@Thickness 0.0787 in
GWFI; IEC 60695-2-12
875 °C

@Thickness 1.00 mm
1610 °F

@Thickness 0.0394 in
GWIT; IEC 60695-2-13
875 °C

@Thickness 1.50 mm
1610 °F

@Thickness 0.0591 in
GWIT; IEC 60695-2-13
875 °C

@Thickness 2.00 mm
1610 °F

@Thickness 0.0787 in
GWIT; IEC 60695-2-13
875 °C

@Thickness 3.00 mm
1610 °F

@Thickness 0.118 in
GWIT; IEC 60695-2-13
875 °C

@Thickness 4.00 mm
1610 °F

@Thickness 0.157 in
GWIT; IEC 60695-2-13
930 °C

@Thickness 3.00 mm
1710 °F

@Thickness 0.118 in
GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
IEC 60250
3.1

@Frequency 100 Hz
3.1

@Frequency 100 Hz
IEC 60250
Dielectric Strength 34.0 kV/mm

@Thickness 1.00 mm
864 kV/in

@Thickness 0.0394 in
IEC 60243-1
Dissipation Factor 0.00050

@Frequency 100 Hz
0.00050

@Frequency 100 Hz
IEC 60250
0.0090

@Frequency 1.00e+6 Hz
0.0090

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 125 V
125 V
CTI M; Solution B; IEC 60112
250 V
250 V
Solution A; IEC 60112