Polymer Property : Modulus of Elasticity = 30200 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	208 GPa @Temperature 90.0 Â°C	30200 ksi @Temperature 194 Â°F
Haynes HR-160Â® alloy plate, aged 4000 hours at 649Â°C (1200Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity	208 GPa @Temperature 90.0 Â°C	30200 ksi @Temperature 194 Â°F
Haynes HR-160Â® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity	208 GPa @Temperature 90.0 Â°C	30200 ksi @Temperature 194 Â°F
Haynes HR-160Â® alloy, plate, aged 1000 hours at 760Â°C (1400Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity	208 GPa @Temperature 90.0 Â°C	30200 ksi @Temperature 194 Â°F
Haynes HR-160Â® alloy, plate, aged 1000 hours at 871Â°C (1600Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity	208 GPa @Temperature 90.0 Â°C	30200 ksi @Temperature 194 Â°F
Haynes HR-160Â® alloy, plate, aged 4000 hours at 760Â°C (1400Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, 10% cold reduction, 1010Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, 20% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, 20% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, 20% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, 40% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, 40% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, cold rolled and 1050Â°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, plate after 16000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, plate after 16000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, plate after 16000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, plate after 4000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, plate after 8000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity	208 GPa @Temperature 200 Â°C	30200 ksi @Temperature 392 Â°F
Haynes HastelloyÂ® B-3Â® alloy, 20% cold work The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Modulus of Elasticity	208 GPa @Temperature 200 Â°C	30200 ksi @Temperature 392 Â°F
Haynes HastelloyÂ® B-3Â® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Modulus of Elasticity	208 GPa	30200 ksi
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed + 10% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t..
Modulus of Elasticity	208 GPa	30200 ksi
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed + 15% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t..
Modulus of Elasticity	208 GPa	30200 ksi
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed + 40% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of ..
Modulus of Elasticity	208 GPa	30200 ksi
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed + 50% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of ..
Modulus of Elasticity	208 GPa	30200 ksi
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed 1950Â°F (1070Â°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950Â°F (1070Â°C)/5 minutes/AC. This produces ASTM grain size 9.5. Other property values are ty..
Modulus of Elasticity	208 GPa	30200 ksi
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed 1950Â°F (1070Â°C) + Aged 1400Â°F (760Â°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950Â°F (1070Â°C)/5 minutes/AC + Aged 1400Â°F (760Â°C)/100h/AC. This produces ASTM grain siz..
Modulus of Elasticity	208 GPa	30200 ksi
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed 2150Â°F (1180Â°C) + Aged 1200Â°F (650Â°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150Â°F (1180Â°C)/5 minutes/AC + Aged 1200Â°F (650Â°C)/100h/AC. This produces ASTM grain siz..
Modulus of Elasticity	208 GPa	30200 ksi
China-Yixing Longly Refractories Zirconia Ceramics LONGLY provides a multitude of zirconia products including balls, plates, tubes, rods and etc. by adopting magnesia, calcia or yttria stabilized zirconia powder as raw material through dry pressing,..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Modulus of Elasticity	208 GPa @Temperature 232 °C	30200 ksi @Temperature 450 °F	Annealed
Latrobe MP159® Alloy MP159 is an alloy of the Multiphase family of alloys possessing the unique combination of ultra-high strength, ductility and corrosion resistance. Through work strengthening and aging, MP159 alloy ..
Modulus of Elasticity	208 GPa	30200 ksi	RT
Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..