Polymer Property : Modulus of Elasticity = 537 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	3.70 - 20.7 GPa	537 - 3000 ksi	Average value: 6.36 GPa Grade Count:13
Overview of materials for Polyetheretherketone, PEEK, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PEEK, Aramid Fiber Filled". Each property range of values reported is minimum and ..
Modulus of Elasticity	3.70 - 12.9 GPa	537 - 1870 ksi	Average value: 8.84 GPa Grade Count:52
Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% ar..
Modulus of Elasticity	3.70 - 13.1 GPa	537 - 1900 ksi	Average value: 8.03 GPa Grade Count:45
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of..
Modulus of Elasticity	3.70 GPa	537 ksi
Lehmann & Voss LUVOCOMÂ® 1105-7568/GY PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Superheated steam sterilizable.High chemical resistance parts, hydrolysis resistance, non ..
Modulus of Elasticity	3.70 GPa	537 ksi
Lehmann & Voss LUVOCOMÂ® 1105-8320 PEEK, with aramid reinforcement and PTFE, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts.Improved friction and wear behaviour. Emergency r..
Modulus of Elasticity	3.70 GPa	537 ksi
Lehmann & Voss LUVOCOMÂ® 1106-8087/BL Polyether imide, unreinforced, laser markable Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le..
Modulus of Elasticity	3.70 GPa	537 ksi	ISO 527
GEHR Plastics PET Polyethylene Terephthalate Polyethylene terephthalate shows high tensile and mechanical strength, hardness and toughness, low friction and a high dimensional stability. PET may be used at temperatures ranging from -20Â°C to..
Modulus of Elasticity	3.70 GPa	537 ksi	Sample Type 1B, 50 mm/min; ISO 527-1/2:1993
Global EPP PA 66E Extruded Polyamide 66 Polyamides, commonly referred to as nylons, are macromolecular, partially crystalline thermoplastics. Their physical properties are mainly determined by the composition and structure of their molecu..
Modulus of Elasticity	3.70 GPa	537 ksi	Sample Type 1B, 50 mm/min; ISO 527-1/2:1993
Global EPP PET PET is an unreinforced, semi-crystalline thermoplastic polyester, demonstrating dimensional stability similar to acetal, combined with the comparable wear resistance of nylon. Heavily loaded mechani..
Modulus of Elasticity	3.70 GPa	537 ksi
Lehmann & Voss LUVOCOMÂ® 1105/WT106 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan..
Modulus of Elasticity	3.70 GPa	537 ksi	Sample Type 1B, 50 mm/min; ISO 527-1/2:1993
Global EPP PA 612 Copolymer Cast Polyamide 612 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Modulus of Elasticity	3.70 GPa	537 ksi	ISO 527-2
Tisan TISLAMID® 6 Flame Retardant (V0) Heat Stabilized Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec..
Modulus of Elasticity	3.70 GPa	537 ksi	TD; ExxonMobil Method
ExxonMobil Metallyte™ 15MM348 OPP Film Product Description: An enhanced barrier metalized film with a very broad seal range and can be considered a multipurpose film. This designed of this film allow excellent performance on HFFS machine..
Modulus of Elasticity	3.70 GPa	537 ksi	TD; ExxonMobil Method
ExxonMobil Metallyte™ 18MM348 OPP Film Product Description: An enhanced barrier metalized film with a very broad seal range designed to be used in laminate with OPP or Polyester for HFFS applications. The design of this film allows excel..
Modulus of Elasticity	3.70 GPa	537 ksi	TD; ExxonMobil Method
ExxonMobil Metallyte™ 18MM483 OPP Film Product Description: A biaxially oriented polypropylene film, metalized on one side with a broad seal range surface on the other side. This film is designed for high barrier performance packaging ap..
Modulus of Elasticity	3.70 GPa	537 ksi	ISO 178
Addiplast Addilene J 520 M40 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast.
Modulus of Elasticity	3.70 GPa	537 ksi	Conditioned; ISO 178
Addiplast Addinyl A2 M20 V10 Nylon 66, Glass/Mineral Filled Mixed products with improved stiffness and good dimensional stability, low warpage.Information provided by Addiplast.
Modulus of Elasticity	3.70 GPa	537 ksi	ASTM D638
Owens Corning Glass Fiber Reinforced Polypropylene, 20 wt.% glass Polypropylene provides good resistance to acids, alkalis and organic solvents even at higher temperatures. It is, however, soluble in chlorinated hydrocarbons. Data provided by the manufacturer, Ow..