Polymer Property : Flexural Strength = 19400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	134 MPa	19400 psi	1.3 mm/min; ASTM D790
PolyOne Edgetek® X PS-154200101 WHITE Polybutylene Terephthalate (PBT) Information provided by PolyOne
Flexural Strength	134 MPa	19400 psi	ASTM D790
SABIC Innovative Plastics Lexan® LGN1500 PC (Asia Pacific)
Flexural Strength	134 MPa	19400 psi	ASTM D790
PolyOne Edgetek® XT XT-115GF-AX01-HF PC+PBT with Glass Fiber Reinforcement (discontinued **) EDGETEK™ XT High Performance Polymers are polycarbonate and polyester alloys that combine strength, durability and chemical resistance. The Edgetek XT product family includes a complete line of gen..
Flexural Strength	134 MPa	19400 psi	ASTM D790
Solvay Specialty Polymers AvaSpire® AV-848 Polyaryletherketone (PAEK) (Unverified Data**) AvaSpire® AV-848 is a high-temperature, polyaryletherketone (PAEK) that offers several key performance advantages over comparable grades of PEEK above 150°C, including better dimensional stability..
Flexural Strength	134 MPa	19400 psi	ASTM D790
Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK) (Unverified Data**) Ketaspire KT-820 SL10 is a polyetheretherketone (PEEK) based compound designed to offer enhanced lubricity and reduced friction compared to standard PEEK. Unlike other grades formulated for wear res..
Flexural Strength	134 MPa	19400 psi	ISO 178
Solvay Specialty Polymers KetaSpire® KT-880 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-880 is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in pellet form. KetaSpire PEEK is produced to the highest industry standards and is characterized by a dist..
Flexural Strength	134 MPa	19400 psi	ASTM D 790
SABIC Innovative Plastics Lexan® 3412 PC (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	134 MPa @Temperature 22.8 °C	19400 psi @Temperature 73.0 °F	ASTM D790
Ensinger Sintimid™ V 15% graphite Polyimide (PI) (discontinued **) SINTIMID™ V polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an idea choice for the most demanding applications. SINTIMID™ V..
Flexural Strength	134 MPa	19400 psi	ASTM D790
LG Chemical IH830A PMMA, General Purpose Grade for Injection Molding Highest of all grades in heat resistanceMechanical strength and surface hardnessParticularly recommended for tail lamp, reflectors, and general lighting fixturesFeatures: Excellent transparency and ..
Flexural Strength	134 MPa	19400 psi
Haysite H-193 Corrosion Resistant Polyester/Glass Sheet A fiber glass reinforced thermoset polyester sheet having good corrosion resistance to numerous acids and alkalis. This material also exhibits a high level of flame retardancy and low smoke generati..
Flexural Strength	134 MPa	19400 psi	ASTM D790
Solvay Specialty Polymers AvaSpireÂ® AV-848 Polyaryletherketone (PAEK) AvaSpireÂ® AV-848 is a high-temperature, polyaryletherketone (PAEK) that offers several key performance advantages over comparable grades of PEEK above 150Â°C, including better dimensional stabi..
Flexural Strength	134 MPa	19400 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DDF029 PC (Asia Pacific) LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant, Glass Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	134 MPa	19400 psi	ASTM D790
Solvay Specialty Polymers KetaSpireÂ® KT-820 SL10 Polyetheretherketone (PEEK) KetaSpireÂ® KT-820 SL10 is a polyetheretherketone (PEEK) based compound designed to offer enhanced lubricity and reduced friction compared to standard PEEK. Unlike other grades formulated for wear..
Flexural Strength	134 MPa	19400 psi	ISO 178
Solvay Specialty Polymers KetaSpireÂ® KT-880 Polyetheretherketone (PEEK) KetaSpireÂ® KT-880 is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in pellet form. KetaSpireÂ® PEEK is produced to the highest industry standards and is characterized b..
Flexural Strength	134 MPa	19400 psi	ISO 178
Solvay Specialty Polymers KetaSpireÂ® KT-880FP Polyetheretherketone (PEEK) KetaSpireÂ® KT-880FP is the high-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural color fine powder form for compression molding and other uses that can benefit from th..
Flexural Strength	134 MPa	19400 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66 LNP* STAT-KON* RFD03 is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material is: Electrically Conductive.
Flexural Strength	134 MPa	19400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to..
Flexural Strength	134 MPa	19400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Asia Pacific) Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to..
Flexural Strength	134 MPa	19400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to..
Flexural Strength	134 MPa	19400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10 LNP* LUBRICOMP* QFL32 is a compound based on Nylon 6/10 containing 10% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
Flexural Strength	134 MPa	19400 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DDF029 PC LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon, Glass Fiber. Added features of this material include: Electrically Conductive. Flame Retardant.
Flexural Strength	134 MPa	19400 psi	GB/9341
Zhejiang Juner PA66-301-G10 Flame-Retardant & Glass Reinforced, Environmental PA66 Applications: Electric Appliance PedestalInformation provided by Zhejiang Juner New Materials Co, Ltd.
Flexural Strength	134 MPa @Temperature 23.0 °C	19400 psi @Temperature 73.4 °F	EN ISO 178
Ensinger TECASINT 4201 SD Polyimide, Black, Carbon Fiber (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Flexural Strength	134 MPa	19400 psi	ASTM D790
Ensinger DELRIN® 507 Black Acetal Homopolymer (POM) Delrin® 507 is a general purpose homopolymer acetal containing a UV stabilizer ideally suited for outdoor applications or those in which there is an otherwise abundant source of UV light.General hi..
Flexural Strength	134 MPa	19400 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 628 Nylon 6/6, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	134 MPa	19400 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOTUF WF003I Polyester, TP LNP THERMOTUF* WF003I is a compound based on Polyester, TP resin containing Glass Fiber. Added features of this material include: High Impact.
Flexural Strength	134 MPa	19400 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 627 Nylon 6/6, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.