Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
Solvay Specialty Polymers AvaSpire® AV-722 SL30 Polyaryletherketone (PAEK)
(Unverified Data**) AV-722 SL30 is a wear resistant grade of AvaSpire polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to the outstanding wea.. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp PFL34 PA 6 LNP* Lubricomp* PFL34 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Am.. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
Solvay Specialty Polymers AvaSpire® AV-722 SL30 Polyaryletherketone (PAEK) AV-722 SL30 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to the outstanding.. |
|||
Flexural Strength | 209 MPa | 30300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon EX08308C PEI (Asia Pacific) Stat-Kon* EX08308C is a high cleanliness Polyetherimide Compound reinforced with Carbon Fiber for use in applications requiring the highest level of cleanliness. This compound is compounded using LN.. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF006E PES LNP* THERMOCOMP* JF006E is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK LNP* THERMOCOMP* LF003 is a compound based on Polyetheretherketone resin containing 15% Glass Fiber. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK (Asia Pacific) LNP* Thermocomp* LF003 is a compound based on Polyetheretherketone resin containing Glass Fiber. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp LF003E PEEK LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp LF003E PEEK (Asia Pacific) LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66 LNP* THERMOCOMP* RFB66 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 30% Glass Bead. |
|||
Flexural Strength | 209 MPa | 30300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON MV00AS PP (Europe-Africa-Middle East) LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled, heat stabilized |
|||
Flexural Strength | 209 MPa | 30300 psi | GB/9341 |
Zhejiang Juner PA66-301-HG30 Flame-Retardant & Glass Reinforced, Environmental PA66 Applications: Connector AS PedestalInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Flexural Strength | 209 MPa @Temperature 23.0 °C |
30300 psi @Temperature 73.4 °F |
EN ISO 178 |
Ensinger TECASINT 1101 Polyimide (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
SABIC Innovative Plastics LNP Verton WV007XXP PBT (Europe-Africa-Middle East) LNP VERTON* WV007XXP is a compound based on Polybutylene Terephalate resin containing Long Glass.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF006EXZ PES LNP* THERMOCOMP* JF006EXZ is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding. |