Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 205 MPa | 29700 psi | STN EN ISO 178 |
Plastcom PLASTAMID® 66 GF 20 PA66 reinforced with glass fiber PA66 for injection molding, reinforced with 20% glass fiber, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, .. |
|||
Flexural Strength | 205 MPa | 29700 psi | STN EN ISO 178 |
Plastcom SLOVAMID 6 GF 30 FRG 5 Polyamide 6, 30% Glass Fiber, Halogen Free Flame Retardant FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fiber, with halogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6mm, glow wire at 960°C,.. |
|||
Flexural Strength | 205 MPa | 29700 psi | STN EN ISO 178 |
Plastcom SLOVAMID® 6 GF 25 FRC 4 PA6 reinforced with glass fiber, flame retarded PA 6 for injection molding, reinforced with 25 % glass fiber, flame retarded with halogen free flame retardant. Main features: flammability according to UL 94 3 at 1,6mm, glow wire at 960°C. Applic.. |
|||
Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
Radici Radiflam® ARV350 AF (dry) Nylon 66 PA66 Self-extinguishing glass-fiber reinforced with phosphorousInformation provided by Radici group. |
|||
Flexural Strength | 205 MPa | 29700 psi | ASTM D 790 |
SABIC Innovative Plastics Lexan® LCG0820 PC (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 205 MPa @Temperature 22.8 °C |
29700 psi @Temperature 73.0 °F |
ASTM D790 |
Ensinger Sintimid™ V Unfilled Polyimide (PI)
(discontinued **) SINTIMID™ V polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an idea choice for the most demanding applications. SINTIMID™ V.. |
|||
Flexural Strength | 205 MPa | 29700 psi | |
Lehmann & Voss LUVOCOM® 1301-7953 PPS, linear, with carbon fiber and PTFE Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts w.. |
|||
Flexural Strength | 205 MPa @Temperature 538 °C |
29700 psi @Temperature 1000 °F |
|
McDanel Advanced Ceramics AP 35 99% Alumina Information provided by McDanel Advanced Ceramic Technologies |
|||
Flexural Strength | 205 MPa | 29700 psi | ASTM D790 |
Kuraray Genestarâ„¢ G1300H Nylon, 30% Glass Filled Standard HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. It is suitable for use in .. |
|||
Flexural Strength | 205 MPa | 29700 psi | |
Lehmann & Voss LUVOCOM® 1105-8389/BL PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension.. |
|||
Flexural Strength | 205 MPa | 29700 psi | 2mm/min; ASTM D790 |
Kingfa PET-G30 30% Glass Fiber Reinforced PET Features:High strengthGood heat resistanceApplications:Injection moldingApplication partsAuto partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Flexural Strength | 205 MPa | 29700 psi | |
Lehmann & Voss LUVOCOM® 1100-8049 Polyether sulfone, with glass fiber Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta.. |
|||
Flexural Strength | 205 MPa | 29700 psi | ASTM D790 |
Solvay Technyl® A20V25 25% Glass Filled, V-0 Nylon 66 Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
Flexural Strength | 205 MPa | 29700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 8032UX PBT+PET (Europe-Africa-Middle East) VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin.. |
|||
Flexural Strength | 205 MPa | 29700 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF006ER PC LNP THERMOCOMP* DF006ER is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF005 PA 66 LNP* THERMOCOMP* RF005 is a compound based on Nylon 66 resin containing 25% Glass Fiber. |
|||
Flexural Strength | 205 MPa | 29700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF008 PC LNP THERMOCOMP* DF008 is a compound based on Polycarbonate resin containing 40% Glass Fiber. |
|||
Flexural Strength | 205 MPa | 29700 psi | ASTM D790 |
A. Schulman SCHULADUR® B GF25LB 25% Glass Fiber Reinforced, Lubricated PET Information provided by A. Schulman. |
|||
Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
Polyplastics Duracon® CH-20 Acetal Co-polymer (POM), Conductive, CF reinforced, Wear resistance DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
Flexural Strength | 205 MPa | 29700 psi | ASTM D790 |
A. Schulman SCHULADUR® B GF25LB 25% Glass Fiber Reinforced, Lubricated PET Information provided by A. Schulman. |
|||
Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
Polyplastics Duranex® 702MS Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
Vyncolit BXE7665 Glass Filled Phenolic Molding Compound Novolac resin based, mainly glass fiber filled. Excellent electrical properties combined with very good mechanical properties. Grade especially suitable for electrical applications.Information pro.. |
|||
Flexural Strength | 205 MPa | 29700 psi | ASTM D790 |
A. Schulman SCHULADUR® B GF25LB 25% Glass Fiber Reinforced, Lubricated PET Information provided by A. Schulman. |
|||
Flexural Strength | 205 MPa | 29700 psi | dry; ISO 178 |
DSM Novamid® 1010GN2-20 NAT/BK37 PA6-GF20 FR(17) 20% Glass Reinforced, Flame Retardant |
|||
Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
Ascend Performance Materials Vydyne® R535 Nylon 66, 35% Glass Reinforced, Conditioned Vydyne® R535 is general-purpose, hydrolysis-resistant, 35% glass-fiber reinforced PA66 resin. This product is lubricated for improved flow and offers superior surface appearance. Glass-reinforced V.. |
|||
Flexural Strength | 205 MPa | 29700 psi | ISO 178 |
BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Conditioned) Ultramid B3G8 BK00564 is a 40% glass filled, pigmented black, injection molding PA6 grade. |