Plastcom SLOVAMID 6 GF 30 FRG 5 Polyamide 6, 30% Glass Fiber, Halogen Free Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVAMID 6 GF 30 FRG 5 Polyamide 6, 30% Glass Fiber, Halogen Free Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fiber, with halogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6mm, glow wire at 960°C, CTI 300. Application for the electrical industry: protectors, coil forms, covers, terminals. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.0072 cm/cm | 0.0072 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0087 cm/cm | 0.0087 in/in | STN 64 0808 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 165 MPa | 23900 psi | STN EN ISO 527-2 |
| Elongation at Break | 2.0 % | 2.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | STN EN ISO 527-2 |
| Flexural Strength | 205 MPa | 29700 psi | STN EN ISO 178 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -20.0 °C |
28.6 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -20.0 °C |
2.38 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | STN EN ISO 75/A |
| Vicat Softening Point | 210 °C | 410 °F | B; STN EN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |
| Glow Wire Test | 960 °C | 1760 °F | STN IEC 60695-2-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | STN IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | STN IEC 60093 |
| Dielectric Strength | 60.0 kV/mm | 1520 kV/in | STN IEC 60243 |
| Comparative Tracking Index | 550 V | 550 V | STN 34 6468 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.15 % | 0.15 % | STN EN ISO 960 |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi |