Polymer Property : Flexural Strength = 325 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	325 MPa	47100 psi
Plastcom SLOVAMID 6 GF 65 PA6, 65% glass fibre FeaturesPA 6 for injection moulding, chemically strengthened with 65% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-good..
Flexural Strength	325 MPa	47100 psi
Lehmann & Voss LUVOCOMÂ® 19-7278 Polyamide 46, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp..
Flexural Strength	325 MPa	47100 psi
Lehmann & Voss LUVOCOMÂ® 19-8365 Polyamide 46, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp..
Flexural Strength	325 MPa	47100 psi	ISO 178
Grupo Repol DinalonÂ® A1S25 G50 PA66 50% Glass Fiber Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Flexural Strength	325 MPa	47100 psi	ISO 178
Solvay Specialty Polymers AmodelÂ® A-4145 HH Polyphthalamide (PPA), 45% Glass Fiber (Dry) AmodelÂ® A-4145 HH is a 45% glass fiber reinforced heat stabilized grade of polyphthalamide (PPA) that has been designed to provide outstanding property retention to thermal oxidative degradation ..
Flexural Strength	325 MPa	47100 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP LC006 PEEK LNP THERMOCOMP* LC006 is a compound based on Polyetheretherketone resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	325 MPa	47100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP QC006 PA6.10 LNP THERMOCOMP* QC006 is a compound based on Nylon 6/10 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	325 MPa	47100 psi	ISO 178
Unitika A1030GFL45 PA6, 45% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd.
Flexural Strength	325 MPa	47100 psi	ISO 178-93
Wellman Wellamid® GF60-66/6 XE-NBK1 60% Glass Fiber Reinforced, Engineering Grade Nylon 66/6 Description: Glass Fiber Reinforced, Engineering Grade Nylon 66/6Information provided by Wellman.
Flexural Strength	325 MPa	47100 psi	ISO 178-93
Wellman Wellamid® GFX1743-N1(PTFE) 45% Glass Fiber Reinforced, Enhanced Lubrication Nylon 66/6 Description: Glass Fiber Reinforced, Enhanced Lubrication Nylon 66/6Information provided by Wellman.
Flexural Strength	325 MPa	47100 psi	2 [mm/min]; ISO 178
Akro-Plastic Akroloy® PA GF 40 (2845) PA 6.6 & PA6I/6T Dry, 40% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param..
Flexural Strength	325 MPa	47100 psi	ISO Data
BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Dry) Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensio..
Flexural Strength	325 MPa	47100 psi	Dry; ASTM D790
Asahi Kasei Leona® 14G33 33% Glass Filled Nylon 66 Enhanced strength and stiffness; with 33% GF. Superior heat aging resistance, fatigue resistance, and creep resistance.Applications:Mechanical and electrical parts, engine mounts and other under-the..