BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. It is available in natural, black, weather resistance and pigmented versions.
Physical Properties Metric English Comments
Density 1.2784 g/cc
0.046185 lb/in³
Melt; ISO 1183
1.49 g/cc
0.0538 lb/in³
ISO 1183
Water Absorption 0.90 %
0.90 %
24 hour; ISO Test
5.2 %
5.2 %
ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
23°C/50% R.H.; ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM Test
Tensile Strength at Break 230 MPa
33400 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 215 MPa
31200 psi
5mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
0.2 in/min; ASTM Test
3.0 %
3.0 %
5mm/min; ISO 527
Tensile Modulus 13.5 GPa
1960 ksi
1mm/min; ISO 527
Flexural Strength 325 MPa
47100 psi
ISO Data
352 MPa
51100 psi
ASTM Test
138 MPa

@Temperature 120 °C
20000 psi

@Temperature 248 °F
ASTM Test
160 MPa

@Temperature 93.0 °C
23200 psi

@Temperature 199 °F
ASTM Test
220 MPa

@Temperature 65.0 °C
31900 psi

@Temperature 149 °F
ASTM Test
450 MPa

@Temperature -40.0 °C
65300 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 11.4 GPa
1650 ksi
ISO Data
11.7 GPa
1700 ksi
ASTM Test
4.83 GPa

@Temperature 120 °C
701 ksi

@Temperature 248 °F
ASTM Test
7.00 GPa

@Temperature 65.0 °C
1020 ksi

@Temperature 149 °F
ASTM Test
Izod Impact, Notched 1.34 J/cm

@Thickness 3.17 mm
2.51 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
ISO Test
11.0 kJ/m²

@Temperature -40.0 °C
5.23 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact Unnotched 9.00 J/cm²
42.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 2.10 J/cm²
9.99 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 31.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
17.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 32.0 µm/m-°C
17.8 µin/in-°F
ISO 11359
CTE, linear, Transverse to Flow 79.0 µm/m-°C
43.9 µin/in-°F
ISO 11359
Specific Heat Capacity 2.522 J/g-°C
0.6028 BTU/lb-°F
Melt
Thermal Conductivity 0.329 W/m-K
2.28 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75
212 °C
414 °F
ASTM Test
Flammability, UL94 HB
HB
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat