Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
PolyOne LubriOne™ NN-30GF/10T WHT Polyamide 66 (Nylon 66) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
LNP Stat-Kon® PDX-E-99689 CCS Polyetherimide, Carbon Fiber Reinforcement
(discontinued **) Features: Low to None Ion Content, Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued.. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
LNP Thermocomp® EF-1004 BK8-115 Polyetherimide, Glass Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
Mitsui AURUM® JGN3030 Thermoplastic Polyimide Resin, Amorphous
(discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i.. |
|||
Flexural Strength | 241 MPa | 35000 psi | 73°F; ASTM D790 |
Ravago Manufacturing Americas Hylon® N1035HLHR Nylon 6/6 (DAM)
(discontinued **) Information provided by Ravago. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP IFL36 PA6.12 LNP LUBRICOMP* IFL36 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS (Asia Pacific) LNP* Lubricomp* OCP36 is a compound based on Polyphenylene Sulfide resin containing Carbon Fiber, Lubricants, Bearing Grade. Added features of this material include: Internally Lubricated, Electric.. |
|||
Flexural Strength | 241 MPa | 35000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2410 PEI 40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 241 MPa | 35000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2410R PEI 40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
Techmer ES Electrafil® J-1305/CF/20 PPS |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF33 HS L BK001 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc.. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP EF006ER PEI LNP* Thermocomp* EF006ER is a compound based on Polyetherimide resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
Flexural Strength | 241 MPa | 35000 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF004H PA 66 LNP* THERMOCOMP* RF004H is a compound based on Nylon 66 containing 20% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF VC006 Super Tough PA 6/6 (Asia Pacific) LNP* THERMOTUF* VC006 is a compound based on Super Tough Nylon 6/6 resin containing Carbon Fiber. Added features of this material include: High Impact. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
Flexural Strength | 241 MPa | 35000 psi | 4 point |
COI Ceramics Sylramic™ S400 Silicon Carbide Ceramic Matrix Composite, Carbon Description: Engineered ceramic composite structures for a broad range of industries and applications.Reinforcing Fiber Flexibility: S400 - Carbon Preceramic Polymer Matrix Precursors: S400 - Crysta.. |
|||
Flexural Strength | 241 MPa | 35000 psi | Lengthwise; ASTM D790 |
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 1/8" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Flexural Strength | 241 MPa | 35000 psi | |
Aremco AREMCOLOX™ 502-676 Machinable Magnesium Oxide Full-fired, fine grain, high purity MgO ceramic. Inert to molten metals, slags, superconductors. Broad line of standard crucibles. Custom parts made to print. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Lubricomp DCL36 PC LNP LUBRICOMP* DCL36 is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP fo.. |
|||
Flexural Strength | 241 MPa | 35000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP VERTON RV0079 PA 66 LNP VERTON* RV0079 is a compound based on Nylon 66 resin containing 35% Long Glasss Fiber. Added features of this material include: Flame Retardant, Structural. |
|||
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP QCL349 PA6.10 LNP* LUBRICOMP* QCL349 is a compound based on Nylon 6/10 resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Flame Retardant, Electrically Conducti.. |