Polymer Property : Flexural Strength = 41000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	283 MPa	41000 psi	1.3 mm/min; ASTM D790
PolyOne LubriOne™ SF2-30CF/15T Natural Polyphenylene Sulfide (PPS) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Flexural Strength	283 MPa	41000 psi	ASTM D790
Network Polymers Nylon 66G33L Description: Black NylonInformation provided by Network Polymers Inc.
Flexural Strength	283 MPa	41000 psi	ASTM D790
Niche Polymer PA6GF43BK Nylon 6, 43% Glass Fiber Filled Information provided by Niche Polymer
Flexural Strength	283 MPa	41000 psi	ASTM D790
Niche Polymer PA6GF50BK Nylon 6, 50% Glass Fiber Filled Information provided by Niche Polymer
Flexural Strength	283 MPa @Temperature 23.9 °C	41000 psi @Temperature 75.0 °F	Dry; ASTM D790
Park Electrochemical Nelcote® S-860 Silicone Prepreg, 1581-112NPH E-Glass Reinforced Nelcote® S-860 is a MIL-P-25518 type silicone resin with a good combination of electrical and high temperature properties. GMS4001 qualified specificationsKey Features and Benefits:500°F maximum s..
Flexural Strength	283 MPa	41000 psi	ASTM D790
PolyOne Edgetek® SF2-40CF/000 NATURAL Polyphenylene Sulfide (PPS) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Flexural Strength	283 MPa	41000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP EX10404H PEI LNP* LUBRICOMP* EX10404H is a compound based on Polyetherimide containing proprietary fillers. Added features of this grade include: Wear Resistant, Healthcare.
Flexural Strength	283 MPa	41000 psi	ASTM D790
Techmer ES HiFillÂ® PA4/6 CF30 30% Carbon Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 30% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedInformation provided by TP Composites..
Flexural Strength	283 MPa	41000 psi	ASTM D790
Techmer ES HiFillÂ® PA6 GF50 RM LE 50% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: LubricantFeatures: Low Extractables, Low Moisture Absorption and LubricatedInf..
Flexural Strength	283 MPa	41000 psi	ASTM D790
Techmer ES HiFillÂ® PET GF45 X 45% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 45% Filler by WeightInformation provided by TP Composites, Inc.
Flexural Strength	283 MPa	41000 psi	ASTM D790
Techmer ES LuriblendÂ® PA4/6 CF30 TL15 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance and Low FrictionInformation p..
Flexural Strength	283 MPa	41000 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP EX93452 PEI LNP THERMOCOMP* EX93452 is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Electrically Conductive.
Flexural Strength	283 MPa	41000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP VERTON RV007SX9 PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV007SX9 is a compound based on PA 66 resin containing Long Glass Fiber.
Flexural Strength	283 MPa	41000 psi	ASTM D790
Teknor Apex ChemlonÂ® 143 G Nylon 66, 43% Short Glass Fiber Reinforced Notes: Flammability: Passes, FMVSS 302 Processing Method: Injection Molding Forms: Pellets FMVSSInformation Provided by Teknor Apex
Flexural Strength	283 MPa	41000 psi	ASTM D790
Chase Plastics CP Pryme® N340HL (Dry) Nylon 6, 40% Glass Fiber Reinforced, Heat Stabilized, Lubricated, Recycled Content Features: Heat stabilizedLubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics.
Flexural Strength	283 MPa	41000 psi	ASTM D790
Chase Plastics CP Pryme® NN133L (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated Features: Good chemical resistanceGrease resistantLubricatedOil resistantHigh rigiditySolvent resistantHigh tensile strengthForm: PelletsApplications: Automotive under the hoodInformation provided b..
Flexural Strength	283 MPa	41000 psi	ASTM D790
Chase Plastics CP Pryme® NN133LUV (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, UV Stabilized Features: Good chemical resistanceGrease resistantLubricatedOil resistantHigh rigiditySolvent resistantHigh tensile strengthGood UV resistanceForm: PelletsApplications: Automotive under the hoodOutd..
Flexural Strength	283 MPa	41000 psi
Anderman Ceramics EA95 Sintered Alumina, 95% Densely sintered alumina is characterized by: high strength and hardness, temperature stability, electrical insulation, and high wear resistance and corrosion resistance even at high temperatures. ..
Flexural Strength	283 MPa	41000 psi	ASTM Test
BASF Ultramid® 1503-2 BK ND3007 33% Glass Filled PA66 (Dry) Ultramid 1503-2 BK ND3007 is a 33% glass reinforced, heat stabilized, pigmented black injection molding PA6/6.
Flexural Strength	283 MPa	41000 psi	ASTM D790
Techmer ES Luriblend® PPA CF30 TL10 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(10%)Features: Lubricated, Good Wear Resistance, High Heat Resistance and Low..