Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | <= 57.0 MPa | <= 8270 psi | ISO 178 |
Polykemi AB POLYblend 45FS GK25 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Ravago Manufacturing Americas Hysun™ 697 ASA Available in North America Features: Good Impact Resistance RoHS CompliantForm: PelletsInformation provided by Ravago |
|||
Flexural Strength | <= 57.0 MPa | <= 8270 psi | ISO 178 |
Polykemi AB POLYfill PPH T1040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | <= 57.0 MPa | <= 8270 psi | ISO 178 |
Polykemi AB POLYfill PPH T2040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Ineos Nova Zylar® 221 Clear Impact Modified Acrylic Copolymer
(discontinued **) Features: High clarityEnhanced mold releaseGood elongationStyrenic processing advantagesExcellent property retention after ETO and gamma sterilization Applications: DisplaysMedical devicesOffice acc.. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Ineos Nova Zylar® 220 Clear Impact Modified Acrylic Copolymer
(discontinued **) Features:High clarity Good elongation Styrenic processing advantages Excellent property retention after gamma and ETO sterilization Meets USP XXIII specifications for Class VI plasticsApplications:D.. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | 0.05 in/min; ASTM D790 |
Ineos Nova Zylar® 220 High Performance Styrenic, Acrylic Copolymer
(discontinued **) Excellent moldability, High clarity, Extended toughness and elongation, meets USP XXI specification for Class VI Plastics, Property retention after gamma irradiationApplications: Display, medical de.. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | at <5% Strain, flexural testing speed of 0.5 inches/minute; ASTM D 790 |
NOVA Chemicals Dylark® FG2500 High-Heat Styrenic Copolymer Product Description and Features: Styrenic copolymer with high-heat resistance, high-impact strength and good toughness. Resins used in food grade sheet extrusion and injection molding application.. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KL002 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KL002 is a compound based on Acetal Copolymer resin containing PTFE. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM Test |
Styrolution Luran® S 797 SE ASA Luran S 797 SE is an extrusion ASA grade with especially high notched impact strength, used for sheet and profile extrusions. The data representable is based on extruded sheet.Information provided .. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MF003AS PP LNP* THERMOCOMP* MF003AS is a compound based on Polypropylene containing 15% Glass Fiber. Characteristics of this grade are: Heat Stabilized. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
SABIC Innovative Plastics NORYL ECN0240 PPE+PS (Asia Pacific) PPE+PS, Auto exterior grade |
|||
Flexural Strength | 57.0 MPa @Strain 3.50 % |
8270 psi @Strain 3.50 % |
ISO 178 |
DuPont Performance Polymers Delrin® 500TE NC010 Acetal (POM)
(Unverified Data**) Toughened Medium Viscosity Acetal Homopolymer with Very Low Emissions Delrin 500TE NC010 (formerly DE20560) is a medium viscosity toughened acetal homopolymer with very low VOC emissions. Processing.. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-747S ABS - Extrusion High Impact Extrusion |
|||
Flexural Strength | 57.0 MPa | 8270 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-764B ABS - Flame Retardant F.R. Weather Resistant |
|||
Flexural Strength | 57.0 MPa | 8270 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-765B ABS - Flame Retardant F.R. Medium Impact |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Aclo Accuguard ABS ABS860V0L Flame Retardant |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Aclo Accutech Polyethylene HD0234G30UVL High Density Glass Reinforced UV Stabilized |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437G20CL Glass Reinforced Coupled |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0336G5M25CL Glass/Mineral Reinforced Coupled |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 300 TF2 POM Tribological modified grade with addition of 10% PTFE, which causes decreased coefficient of friction and wear.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 500 LS POM High flow injection molding grade based on Tarnoform 500 modified with soluble light stabilizers improving weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® X9653 Modified Polyphenylene Ether AutomotiveInformation provided by Asahi Kasei |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
A. Schulman ComAlloy Comshield® 220 ABS, Electrically Conductive - Carbon Black Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 200 LS POM Injection molding grade based on Tarnoform 200 modified with soluble light stabilizers improving weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 200 POM This material is a standard extrusion grade, also could be used for injection molding of low shape complexity details.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Ashley Polymers Ashlene® ABS Resin F-217 General purpose super high impact with good gloss.Data provided by the manufacturer |
|||
Flexural Strength | <= 57.0 MPa | <= 8270 psi | ISO 178 |
Polykemi AB POLYfill PPH T5038 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Ashley Polymers Ashlene® P268WO PPO An extrusion grade for general purpose application requiring flame retardancy and good impact resistance.Data provided by the manufacturer |
|||
Flexural Strength | 57.0 MPa | 8270 psi | ASTM D790 |
Owens Corning Glass Fiber Reinforced Polypropylene, 20 wt.% glass Polypropylene provides good resistance to acids, alkalis and organic solvents even at higher temperatures. It is, however, soluble in chlorinated hydrocarbons. Data provided by the manufacturer, Ow.. |