Polymer Property : Compressive Modulus = 2.70 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Modulus	2.70 GPa	392 ksi	Type B, 5mm/min; ISO 604:2002
Nylacast H.S. Blue Cast Nylon 6, Heat Stabilized HS Blue is a heat Stabilised Cast Nylon 6. Its mechanical properties are maintained when operating at higher temperature and improves mechanical properties. This helps to reduce the stress distortio..
Compressive Modulus	2.70 GPa	392 ksi	Type B, 5mm/min; ISO 604:2002
Nylacast Moly Cast Nylon 6, MoS2 Filled Nylacast Moly is part of the Cast Nylon 6 family. Its improved crystallization occurs by the addition of Molybdenum Disulphide. It includes MoS2, which is an extremely effective self dry lubricant w..
Compressive Modulus	2.70 GPa	392 ksi	Type B, 5mm/min; ISO 604:2002
Nylacast PA6C Cast Nylon 6 Natural PA6 is the base to the other grades of material offered by Nylacast. It is available in Natural (off white) or Black colour. It is made by ionic polymerisation of e-caprolactam under anhydri..
Compressive Modulus	2.70 GPa	392 ksi	ISO 604
Polikim KESTAMID® PA6G Polyamide 6 Kestamid® is also known as Cast Polyamide or Cast Nylon. Kestamid® is an engineering plastic used commonly in all industrial branches for its superior mechanical, physical, chemical and electrical..
Compressive Modulus	2.70 GPa	392 ksi	Sample Type A, 1 mm/min; ISO 604:2002
Global EPP PA 6C Cast Polyamide 6 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Modulus	2.70 GPa	392 ksi	Sample Type A, 1 mm/min; ISO 604:2002
Global EPP PA 6C HS BLUE Cast Polyamide 6 + UV and Heat Stabilizers Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Modulus	2.70 GPa	392 ksi	Sample Type A, 1 mm/min; ISO 604:2002
Global EPP PET SL PET + Solid Lubricant PET is an unreinforced, semi-crystalline thermoplastic polyester, demonstrating dimensional stability similar to acetal, combined with the comparable wear resistance of nylon. Heavily loaded mechani..
Compressive Modulus	2.70 GPa	392 ksi	ISO 604
Polikim KESTAMID® HS Polyamide 6, Heat Resistant Kestamid-HS® is Polikim’s cast polyamide with increased heat resistance. Thermal stabilizer additives increase thermal aging significantly. In operating temperatures over 80°C, it performs with ..
Compressive Modulus	2.70 - 3.00 GPa	392 - 435 ksi	Average value: 2.84 GPa Grade Count:5
Overview of materials for Nylon 6, MoS2 Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, MoS2 Filled". Each property range of values reported is minimum and maximum values of appropria..