Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 23.0 - 63.0 MPa | 3340 - 9140 psi | Average value: 39.4 MPa Grade Count:14 |
Overview of materials for Polypropylene with 20% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Mica Filler". Specific grades with primary filler content between 15% and 24% are.. |
|||
Ball Indentation Hardness | 23.0 - 37.0 MPa | 3340 - 5370 psi | Average value: 32.0 MPa Grade Count:9 |
Overview of materials for Polytetrafluoroethylene (PTFE), Molded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Molded". Each property range of values reported is minimum and maximum v.. |
|||
Ball Indentation Hardness | 23.0 - 28.0 MPa | 3340 - 4060 psi | DIN 53 456 |
Isoflon FEP Fluorinated Ethylene Propylene Fluoropolymer material specifications.Information provided by Isoflon. |
|||
Ball Indentation Hardness | 23.0 - 28.0 MPa | 3340 - 4060 psi | DIN 53 456 |
Isoflon PTFE Polytetrafluoroethylene Fluoropolymer material specifications.Information provided by Isoflon. |
|||
Ball Indentation Hardness | 23.0 MPa | 3340 psi | 132 N/10s; ISO 2039 |
Borealis Daplen™ EF005AE Polypropylene TPO Compound Daplen™ EF005AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, give.. |
|||
Ball Indentation Hardness | >= 23.0 MPa | >= 3340 psi | ISO 2032 |
Adamas Adalon® 902 PTFE, 1% Conductive filler Information provided by Adamas, HPM |
|||
Ball Indentation Hardness | 23.0 - 90.0 MPa | 3340 - 13100 psi | Average value: 49.3 MPa Grade Count:31 |
Overview of materials for Polypropylene, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |