Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 224.1 MPa @Temperature 177 °C |
32500 psi @Temperature 351 °F |
Wet condition - 96 hours in boiling H2O |
Hexcel® HexPly® F650 Bismaleimide Resin with Fiberglass 7781 fabric reinforcement Laminate Physicals: 53% Fiber volume, 29% Resin content, 0.5% VoidsInformation provided by HexCel |
|||
Compressive Yield Strength | 224 MPa @Temperature 163 °C |
32500 psi @Temperature 325 °F |
Open Hole Compression; Wet |
Hexcel® HexPly® 954-2A Curing Cyanate Resin, IM7 Fiber Information provided by HexCel |