Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Creep Strength | 3.70 - 3.70 MPa @Temperature 60.0 - 90.0 °C |
537 - 537 psi @Temperature 140 - 194 °F |
Average value: 3.70 MPa Grade Count:4 |
Overview of materials for Polyvinylidinefluoride (PVDF), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyvinylidinefluoride (PVDF), Molded/Extruded". Each property range of values reported is minimum and m.. |
|||
Creep Strength | 3.70 - 3.70 MPa @Time 360000 - 3.60e+6 sec |
537 - 537 psi @Time 100 - 1000 hour |
Average value: 3.70 MPa Grade Count:4 |
Overview of materials for Polyvinylidinefluoride (PVDF), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyvinylidinefluoride (PVDF), Molded/Extruded". Each property range of values reported is minimum and m.. |
|||
Creep Strength | 3.70 MPa @Temperature 90.0 °C, Time 360000 sec |
537 psi @Temperature 194 °F, Time 100 hour |
Deflection = 3.3%; Flexural Creep |
Arkema Group KYNAR® 1000 HD Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
Creep Strength | 3.70 MPa @Temperature 90.0 °C, Time 3.60e+6 sec |
537 psi @Temperature 194 °F, Time 1000 hour |
Deflection = 3.4%; Flexural Creep |
Arkema Group KYNAR® 1000 HD Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
Creep Strength | 3.70 MPa @Temperature 60.0 °C, Time 360000 sec |
537 psi @Temperature 140 °F, Time 100 hour |
Deflection = 1.5%; Flexural Creep |
Arkema Group KYNAR® 1000 HD Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
Creep Strength | 3.70 MPa @Temperature 60.0 °C, Time 3.60e+6 sec |
537 psi @Temperature 140 °F, Time 1000 hour |
Deflection = 1.7%; Flexural Creep |
Arkema Group KYNAR® 1000 HD Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
Creep Strength | 3.70 MPa @Temperature 90.0 °C, Time 360000 sec |
537 psi @Temperature 194 °F, Time 100 hour |
Deflection = 3.3%; Flexural Creep |
Arkema Group KYNAR® 370 Polyvinylidene Fluoride (PVDF) Homopolymer - Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. Low melt shrinkage, graphite powder filled. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
Creep Strength | 3.70 MPa @Temperature 90.0 °C, Time 3.60e+6 sec |
537 psi @Temperature 194 °F, Time 1000 hour |
Deflection = 3.4%; Flexural Creep |
Arkema Group KYNAR® 370 Polyvinylidene Fluoride (PVDF) Homopolymer - Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. Low melt shrinkage, graphite powder filled. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
Creep Strength | 3.70 MPa @Temperature 60.0 °C, Time 360000 sec |
537 psi @Temperature 140 °F, Time 100 hour |
Deflection = 1.5%; Flexural Creep |
Arkema Group KYNAR® 370 Polyvinylidene Fluoride (PVDF) Homopolymer - Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. Low melt shrinkage, graphite powder filled. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
Creep Strength | 3.70 MPa @Temperature 60.0 °C, Time 3.60e+6 sec |
537 psi @Temperature 140 °F, Time 1000 hour |
Deflection = 1.7%; Flexural Creep |
Arkema Group KYNAR® 370 Polyvinylidene Fluoride (PVDF) Homopolymer - Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. Low melt shrinkage, graphite powder filled. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
Creep Strength | 3.70 MPa @Temperature 90.0 °C, Time 360000 sec |
537 psi @Temperature 194 °F, Time 100 hour |
Deflection = 3.3%; Flexural Creep |
Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness .. |
|||
Creep Strength | 3.70 MPa @Temperature 90.0 °C, Time 3.60e+6 sec |
537 psi @Temperature 194 °F, Time 1000 hour |
Deflection = 3.4%; Flexural Creep |
Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness .. |
|||
Creep Strength | 3.70 MPa @Temperature 60.0 °C, Time 360000 sec |
537 psi @Temperature 140 °F, Time 100 hour |
Deflection = 1.5%; Flexural Creep |
Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness .. |
|||
Creep Strength | 3.70 MPa @Temperature 60.0 °C, Time 3.60e+6 sec |
537 psi @Temperature 140 °F, Time 1000 hour |
Deflection = 1.7%; Flexural Creep |
Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness .. |
|||
Creep Strength | 3.70 MPa @Temperature 90.0 °C, Time 360000 sec |
537 psi @Temperature 194 °F, Time 100 hour |
Deflection = 3.3%; Flexural Creep |
Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
Creep Strength | 3.70 MPa @Temperature 90.0 °C, Time 3.60e+6 sec |
537 psi @Temperature 194 °F, Time 1000 hour |
Deflection = 3.4%; Flexural Creep |
Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
Creep Strength | 3.70 MPa @Temperature 60.0 °C, Time 360000 sec |
537 psi @Temperature 140 °F, Time 100 hour |
Deflection = 1.5%; Flexural Creep |
Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
Creep Strength | 3.70 MPa @Temperature 60.0 °C, Time 3.60e+6 sec |
537 psi @Temperature 140 °F, Time 1000 hour |
Deflection = 1.7%; Flexural Creep |
Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |