Polymer Property : Tensile Strength at Break = 10000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 69.0 MPa
10000 psi
ISO.527 DIN.53455
Omnia Plastica Akulon® POM h Acetal Homopolymer
The general features of homopolymer acetalic resin are similar to those of copolymer POM c, except that service temperature (under load) is slightly higher but resistance to hydrolysis and strong al..
Tensile Strength at Break 68.9 MPa
10000 psi
ASTM D638
Polymer Resources PC-FD3-[color]-1 Polycarbonate, FDA-compliant Feedstocks, High Flow with Mold Release, Gamma Resistant
Polycarbonate, FDA-compliant Feedstocks, High Flow with Mold Release, Gamma ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pig..
Tensile Strength at Break 68.9 MPa
10000 psi
ASTM D638
Polymer Resources PC-G15 Polycarbonate, 15% Glass Reinforced
Polycarbonate, 15% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polym..
Tensile Strength at Break 68.9 MPa
10000 psi
ASTM D638
Polymer Resources PC-GP2-D-[color]-5 Polycarbonate, FDA-compliant Feedstocks, Medium Flow
Polycarbonate, FDA-compliant Feedstocks, Medium FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information ..
Tensile Strength at Break 68.9 MPa
10000 psi
ASTM D638
Polymer Resources PC-GP2-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Medium Flow with Mold Release
Polycarbonate, FDA-compliant Feedstocks, Medium Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sa..
Tensile Strength at Break 69.0 MPa
10000 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® FXE144H PC (Asia Pacific)
FXE144H is a Lexan PC Translucent Grade in our VisualFX Portfolio. It is part of Energy family, which includes Illuminate, Glass, and Flame effects. Grade was developed to meet the Aesthetic Differe..
Tensile Strength at Break 69.0 MPa
10000 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® SLX2432T PC Copolymer (Asia Pacific)
Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors.
Tensile Strength at Break 69.0 MPa
10000 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer
XHT4141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
Tensile Strength at Break 69.0 MPa
10000 psi
ISO 527
Polyplastic Armlen® PP GF MF 30-1 Polypropylene, 30% Glass and Mineral Filled
Injection moldingInformation provided by PolyPlastic Group.
Tensile Strength at Break 68.9 MPa
10000 psi
ASTM D638
Ravago Manufacturing Americas Hylex® P1325L Polycarbonate, UV Stabilized, High Flow, Mold Release
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ente..
Tensile Strength at Break 69.0 MPa
10000 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK (Asia Pacific)
LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 69.0 MPa
10000 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp 2FL24 FP-E (EFTE)
LNP* 2FL24 is a Fluoropolymer, ETFE grade containing Glass Fibers and PTFE.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 68.9 MPa
10000 psi
ASTM D638
PlastxWorld CEVIAN®-N 050 SAN resin
These are typical values and are not intended for specification purposes. UL approved file No. is E47773.Information provided by PlastxWorld Inc.
Tensile Strength at Break 68.9 MPa
10000 psi
ASTM D638
PlastxWorld CEVIAN®-N 055 SAN resin
These are typical values and are not intended for specification purposes. UL approved file No. is E142893. Information provided by PlastxWorld Inc.
Tensile Strength at Break 69.0 MPa
10000 psi
ASTM D638
Unitika LM-8503-10
Chemical resistance, and excellent lubricant propertyInformation provided by Unitika Ltd.
Tensile Strength at Break 69.0 MPa
10000 psi
ASTM D638
Unitika P-1001 Engineering Plastic
P series resins are resins succeeding the characteristics of the neat polymer, U100, and improved in flowability and optical properties. Among many super engineering plastics, the resins are few tra..
Tensile Strength at Break 69.0 MPa
10000 psi
ISO 527
Unitika TERRAMAC HV-6250H Polylactic Acid (PLA)
Foam, Extrusion, blow, and foam sheet grades. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
Tensile Strength at Break 69.0 MPa
10000 psi
chs 2.0 in/min; ASTM D638
Diamond Polymers PC 2418 R UV UV Stabilized/Mold Release Polycarbonate
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength at Break 68.9 MPa
10000 psi
ASTM D638
Polymer Resources PPX-MF-FR3 Modified PPO, UL 94 V-0 with HDT of 230 F, Mineral Reinforced  (Unverified Da
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.