Polymer Property : Tensile Strength at Break = 12.9 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	12.9 MPa	1870 psi	ASTM D1414
Greene Tweed CHEMRAZÂ® 655 Perfluoroelastomer ChemrazÂ® 655 is Greene Tweedâ€™s high-temperature off-white perfluoroelastomer. Specifically developed for wafer processes with operating temperatures up to 315Â°C (600Â°F), Chemraz 655 p..
Tensile Strength at Break	12.9 MPa	1870 psi	ASTM D412
Teknor Apex Telcar® TL-1183A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P..
Tensile Strength at Break	12.9 MPa	1870 psi	ASTM D412
Teknor Apex Telcar® TL-1273A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P..
Tensile Strength at Break	12.9 MPa	1870 psi
Daikin DAI-EL G-575 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 70% Fluorine Content Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: Low permeability to gasoline and a..
Tensile Strength at Break	12.9 MPa	1870 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FC 2261Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2261Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu..
Tensile Strength at Break	12.9 MPa	1870 psi	Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FC 2211 Fluoroelastomer Dyneon FC 2211 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formulations. The "dry" ingre..
Tensile Strength at Break	12.9 MPa	1870 psi	ASTM D412
Teknor Apex APEX® 2565-H Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Good FlexibilityUses-General Purpose, ProfilesAppearance-Natural Color, OpaqueForms-PelletsProcessin..